摘要
Bi5Ti3FeO15 ceramics were synthesized by the solid state reaction. XRD analysis shows a single phase perovskite structure with no impurities identified. Two obvious dielectric anomalies around 1007 and 1090 K were exhibited by this material, indicating that there are two phase transitions. While no peak was found in the curve. In addition, the conduction loss activation energies calculated at 476-639 K, 652-966 K, and 980-1095 K are 0.156, 0.262, and 0.707 eV, respectively. Polarization versus electric field hysteresis loops associated with of 6.08 渭C/cm2 and of 59 kV/cm were obtained.