High-rate fabrication of YBCO coated conductors using TFA-MOD method

详细信息	查看全文 | 推荐本文 |

• 作者：K. Nakaoka ; ^{knakaoka@istec.or.jp} ; M. Yoshizumi ; Y. Usui ; T. Izumi ; Y. Shiohara
• 关键词：YBCO ; TFA-MOD method ; Thick film
• 刊名：Physics Procedia
• 出版年：2012
• 期刊代码：P128_18753892
• 类别：ph
• 出版时间：2012
• 卷：27
• 期：Complete
• 页码：196-199
• 文件大小：515 K

摘要

The YBa2Cu3O7-y (YBCO) coated conductors derived from metal-organic deposition (MOD) method using the metal salts of trifluoroacetic acid (TFA) have been developed with high critical current property. The long-length YBCO coated conductors have been fabricated by multi-turn reel-to-reel system. Increasing the thickness per single coating in the multi-turn reel-to-reel system is a cost-effective technique for fabrication of the precursor films in the calcination process. In this work, we have developed a new starting solution consisting of non-fluorine salts of yttrium 4-oxopentanoate and copper 2-ethylhexanoate with focusing on increasing the thickness per single coating for a high-rate fabrication of the YBCO coated conductors by the TFA-MOD method. The critical thickness per single coating of the film fabricated from the new starting solution was 0.54 渭m/coat. High critical current of 377 A/cm-width with high critical current density (3.0 MA/cm2) was obtained in the YBCO film fabricated on CeO2 buffered LaMnO3/MgO/Gd2Zr2O-7/HastelloyTM substrates using the new starting solution at the thickness per single coating of 0.42 渭m/coat.