摘要
To simulate the corrosion of galvanized steel, artificial zinc rust of zinc hydroxysulfate (Zn4(SO4)(OH)6路nH2O:ZHS路nH2O) was prepared in the presence of Fe(II) and Fe(III) at 85 掳C. Adding Fe(II) and Fe(III) suppressed the crystallization, particle growth and adsorption of corrosive gasses such as CO2 and SO2 on ZHS路nH2O. The effect of Fe(III) was much higher than that of Fe(II). On increasing Fe(III) added, the crystal structure turned following as ZHS路nH2O 鈫?#xA0;a mixture of ZHS路nH2O and 伪-FeOOH 鈫?#xA0;伪-FeOOH and altered the particle morphology from hexagonal plate to needle-like nanoparticles.