Thermal conductivity of mixed alkali silicate glasses at low temperature

详细信息	查看全文 | 推荐本文 |

• 作者：Y. Hiroshima ; Y. Hamamoto ; S. Yoshida ; J. Matsuoka
• 关键词：Phonons ; Medium-range order ; Thermal conductivity
• 刊名：Journal of Non-Crystalline Solids
• 出版年：2008
• 期刊代码：50_00223093
• 类别：ms
• 出版时间：15 January 2008
• 卷：354
• 期：2-9
• 页码：341-344
• 文件大小：125 K

摘要

Thermal conductivity of glass is one of the fundamental properties of it. However, that has not been studied enough. That of only less than 20 compositions has been measured below the room temperature. In this study, we measured the thermal conductivity of xNa₂O · (100 − x)SiO₂ and (33 − y)Na₂O · yCs₂O · 67SiO₂ glasses by a transient heating method in the temperature range from about 150 K to room temperature. The conductivity of xNa₂O · (100 − x)SiO₂ is found to decrease with the increase in alkali content. The dominant factor of this behavior is the decrease in phonon mean free path, which is due to the increase of non-bridge oxygen. Thermal conductivity of (33 − y)Cs₂O · yNa₂O · 67SiO₂ is decreased with the increase in Cs₂O/(Na₂O + Cs₂O) ratio. The dominant factor of this behavior is the decrease of sound velocity. However, composition dependence of the phonon mean free path also affects the thermal conductivity. Phonon mean free path of 33Cs₂O · 67SiO₂ glass is longer than that of 33Na₂O · 67SiO₂ glass, and should be related to the change in distribution of structural unit in glass. In addition, phonon mean free path of mixed alkali glasses are shorter than that of single alkali glasses.