Aging effect on microstructure and hardness of two-phase Ni₃Al-Ni₃V intermetallic alloys containing Ta and Re

详细信息	查看全文 | 推荐本文 |

• 作者：Taku Moronaga ; ^{moronaga@mtr.osakafu-u.ac.jp} ; Seiya Ishii ; Yasuyuki Kaneno ; Hiroshi Tsuda ; Takayuki Takasugi
• 关键词：Ni3Al ; Ni3V ; Multi-phase intermetallics ; Age hardening ; Transmission electron microscopy ; Scanning electron microscopy
• 刊名：Materials Science and Engineering ; A
• 出版年：2012
• 期刊代码：61_09215093
• 类别：ms
• 出版时间：30 March, 2012
• 卷：539
• 期：Complete
• 页码：30-37
• 文件大小：2142 K

摘要

Two-phase intermetallic alloys composed of geometrically closed packed (GCP) Ni₃Al (L1₂ phase) and Ni₃V (D0₂₂ phase) have very attractive mechanical properties at high temperatures and are therefore being considered for use as high temperature structural materials. In this study, it was found that the addition of Ta remarkably enhanced the alloys鈥?hardness due to solid solution hardening in the constituent phases but did not result in an age hardening effect. On the other hand, the addition of Re inhibited the formation of the two-phase microstructure in the solution treated condition, resulting in the lowest hardness. After aging at 1223 K, the Ni solid solution phase in the channel region of the Re-added alloy was decomposed into Ni₃Al and Ni₃V, accompanied by the precipitation of a Re-rich phase. Consequently, the hardness rapidly increased with increasing aging time. Simultaneous addition of Ta and Re induced fine, dense precipitation of Re-rich phase after aging and consequently resulted in higher hardness than the addition of Ta or Re individually.