摘要
In this research, the high silicon–iron strips (near to 6.5%Si) were produced by the direct powder rolling (DPR) technique. The continuous strips could be compacted by rolling from silicon and iron powders and sintered by the following heat treatments. The chemical formula, Fe+Si→Fe (Si)+Fe3Si (Si), controls the reaction of silicon and iron powders. Optimized mechanical properties of the strip due to the composite phase between Fe3Si (Si) and Fe (Si) make the further rolling possible. The soft magnetic properties of final samples were measured in the frequency from 50Hz to 20kHz and the results show that the core loss is relatively lower above 1kHz.