摘要
Giant magnetoresistance was found in DC magnetron sputtering Fe/ITO multilayers. The magnetic properties, electrical properties and magnetoresistance were investigated. A critical temperature is found around 50 K where the temperature dependence of resistivity and magnetoresistance ratio exhibit an abruptly change. The temperature dependence of resistance is found to obey Mott's 1/4 law for low temperature. The max magnetoresistance ratio of 2.0%and 6.7%is found at room temperature and 12.5 K, respectively. The increase of magnetoresistance ratio at low temperature is due to the decrease of spin-mixing effect.