摘要
Thermoelectric (TE) properties such as resistivity (ρ), Seebeck coefficient (S), and thermal conductivity (κ) of Ca4−3xCe3xMn3O10 (0<x≤0.03) polycrystalline samples were measured from room temperature to 1000K. ρ shows an obvious decrease with the increment of Ce content. The hopping conduction mechanism is used to explain the conduction behavior of these samples. The negative S values indicate that these materials are n-type. The sample of x=0.03 has the largest power factor, 0.52×10−4Wm−1K−2 at 1000K. The value of κ and the dimensionless figure of merit of this sample is 1.51Wm−1K−1 and 0.034 at 1000K, respectively.