摘要
The microstructure and mechanical properties of the cast Ti-43.7Al-3.2(Nb,Cr,Mo)-0.2B alloy and聽a Ti-45Al-8Nb-0.2C alloy after hot extrusion followed by heat treatment were studied in the present work. The hot-worked alloy showed appreciably higher strength/ductility properties at room temperature as compared with those of the cast alloy. The difference in the mechanical properties gradually decreased with increasing the test temperature. At 750聽掳C similar strength/ductility properties as well as long-term strength were obtained for both alloys.