Synthesis and structural properties of titanium containing microporous/mesoporous silicate composite (Ti, Al)-Beta/MCM-48

详细信息	查看全文 | 推荐本文 |

• 作者：Matjaž ; Mazaj ; Nata&#x161 ; a Zabukovec Logar ; Gregor Mali ; Nata&#x161 ; a Novak Tu&#x161 ; ar ; Iztok Arč ; on ; Alenka Ristić ; Aleks ; er Reč ; nik ; Venč ; eslav Kauč ; ič
• 关键词：Microporous ; Mesoporous ; Microporous/Mesoporous composite ; (Ti ; Al)-Beta/MCM-48 ; Ti EXAFS ; Ti XANES ; NMR ; Nitrogen adsorption ; HRTEM
• 刊名：Microporous and Mesoporous Materials
• 出版年：2007
• 期刊代码：78_13871811
• 类别：ch
• 出版时间：1 February 2007
• 卷：99
• 期：1-2
• 页码：3-13
• 文件大小：1018 K

摘要

Thermally stable titanium-containing microporous/mesoporous composite (Ti, Al)-Beta/MCM-48 was synthesised hydrothermally in the presence of structure-directing agents cetyltrimethylammonium bromide (CTABr), polyoxyethylene(8) isooctylhexyl ether (Triton^® X-114) and tetraethylammonium hydroxide (TEAOH) in the absence of sodium cations. The presence of both microporous and mesoporous phases was determined by XRD and HRTEM measurements and by the analysis of nitrogen adsorption isotherm based on the α-plot method. The mass percentage (μ) of the microporous material in the composite is approximately 6.5%. NMR investigations showed that acid sites related to framework aluminium were generated by calcination of the as-synthesised (Ti, Al)-Beta/MCM-48. Local environment of titanium incorporated into the microporous/mesoporous silicate material was investigated by X-ray absorption spectroscopy. XANES studies showed the presence of tetrahedrally-coordinated Ti⁴⁺ cations in the template-free sample. EXAFS analysis revealed that titanium cations were coordinated to four oxygens in the first coordination shell, to one oxygen at 1.73(1) Å and three oxygens at 1.86(1) Å. In the second coordination sphere three silicon atoms were found at distances 3.18(2) Å and 3.48(2) Å, respectively. These results indicated framework Ti and thus the presence of Ti oxidation centres within the composite material.