Comparative study on corrosion behavior of as-cast and extruded Mg-5Y-7Gd-1Nd-0.5Zr alloy in 5%NaCl aqueous solution

详细信息	查看全文 | 推荐本文 |

• 作者：Xin ZHANG^a ; ^b ; ^c ; ^{bjzx201@yahoo.com.cn} ; Kui ZHANG^a ; Xing-gang LI^a ; Xia DENG^a ; Hong-wei LI^b ; ^c ; Bao-dong ZHANG^b ; ^c ; Chang-shun WANG^b ; ^c
• 关键词：Mg&ndash ; 5Y&ndash ; 7Gd&ndash ; 1Nd&ndash ; 0.5Zr magnesium alloy ; corrosion morphology ; polarization curve
• 刊名：Transactions of Nonferrous Metals Society of China
• 出版年：2012
• 期刊代码：12_10036326
• 类别：ms
• 出版时间：May, 2012
• 卷：22
• 期：5
• 页码：1018-1027
• 文件大小：2089 K

摘要

The corrosion behaviours of Mg-5Y-7Gd-1Nd-0.5Zr magnesium alloys prepared by as-casting and extrusion were investigated in 5%NaCl aqueous solution by immersion and electrochemical tests. The microstructure indicates the mean grain size of 15 渭m for the extruded and 100 渭m for the as-cast Mg-5Y-7Gd-1Nd-0.5Zr magnesium alloys. The corrosion morphology of as-cast sample shows pitting corrosion and little filiform corrosion, but that of the extruded sample shows pitting corrosion at the initial stage. The corrosion rate of extruded sample is higher than that of as-cast Mg-5Y-7Gd-1Nd-0.5Zr alloy according to the immersion test. The second phases containing RE acting as cathodes improve the corrosion properties. The corrosion potentials of as-cast and extruded Mg-5Y-7Gd-1Nd-0.5Zr alloys are 鈭?.658 V and 鈭?.591 V, respectively. The origins of the distinctive corrosion behavior of as-cast and extruded Mg-5Y-7Gd-1Nd-0.5Zr Mg alloys were discussed.