Preliminary investigations of the production of MgAlON bonded refractories
- 作者：S. Pichlbauer<sup>asup><sup> ; sup><sup>sabine.pichlbauer@unileoben.ac.atsup> ; H. Harmuth<sup>asup> ; Z. Lenč ; é ; š ; <sup>bsup> ; P. Š ; ajgalí ; k<sup>bsup>
- 关键词：Sintering ; Refractories ; MgO ; Al2O3 ; MgAlON
- 刊名：Journal of the European Ceramic Society
- 出版年：2012
- 期刊代码：53_09552219
- 类别：ms
- 出版时间：July, 2012
- 卷：32
- 期：9
- 页码：2013-2018
- 文件大小：1122 K
摘要
The aim of the work was to find an appropriate composition for the formation of MgAlON bonding phase for Al<sub>2sub>O<sub>3sub> and MgO based refractories. The first step was the preparation of pure MgAlON. AlN and Al<sub>2sub>O<sub>3sub> were used as starting powders and either MgO or MgAl<sub>2sub>O<sub>4sub> was added as a source of magnesium. The results verified the possibility to produce MgAlON under the prevailing conditions. Afterwards, MgAlON bonded alumina and magnesia refractories were investigated. The obtained results confirmed the possibility of the production of MgAlON bonded alumina refractories. However, in the case of magnesia-based samples MgAlON was not formed and instead stoichiometric spinel, AlN and alumina rich spinel were detected in the bonding phase. Additionally, the joining between the MgO grains and the matrix was poor with wide gaps on the interface.