Photorefractive properties of polyphosphazenes containing carbazole-based multifunctional chromophores
- 作者：Li Zhang ; Jun Shi ; Zheng Yang ; Maomao Huang ; Zhijian Chen ; Qihuang Gong ; Shaokui Cao
- 关键词：Photorefractive ; Polyphosphazene ; Post-azo-coupling
- 刊名：Polymer
- 出版年：2008
- 期刊代码：83_00323861
- 类别：ms
- 出版时间：15 April 2008
- 卷：49
- 期：8
- 页码：2107-2114
- 文件大小：489 K
摘要
A series of amorphous polyphosphazenes containing carbazole-based multifunctional chromophores were synthesized. These polymers show low glass transition temperature (20–65 °C) and can easily be fabricated into optically transparent films with long-term stability. As an unambiguous evidence of photorefractive effect, preliminary two-beam-coupling experiments were performed at 633 nm under room temperature. All of these single-component polymers exhibited photorefractive performance without external electric field or prepoling, and gain coefficient of 91 cm−1 was observed in a polymer with the lowest glass transition temperature. The influence of the alkylene spacer length between the side group and the polymer backbone on the glass transition temperature, chromophore loading, as well as the optical gain was discussed. The steady-state photorefractive performance of a polyphosphazene with the shortest alkylene spacer was enhanced significantly by adding a photoconductive plasticizer N-ethyl-carbazole to lower the glass transition temperature and a gain of 198 cm−1 and a diffraction efficiency of 46%were achieved at zero electric field.