Microstructures and mechanical properties of Al2O3-C refractories with addition of multi-walled carbon nanotubes
- 作者：Ming Luo ; Yawei Li ; liyaweiwust@hotmail.com ; Shengli Jin ; Shaobai Sang ; Lei Zhao ; Yuanbing Li
- 关键词：MWCNTs ; Graphite flake ; Al2O3-C refractories ; Microstructures ; Mechanical properties
- 刊名：Materials Science and Engineering ; A
- 出版年：2012
- 期刊代码：61_09215093
- 类别：ms
- 出版时间：30 June, 2012
- 卷：548
- 期：Complete
- 页码：134-141
- 文件大小：1939 K
摘要
Microstructures and mechanical properties of Al2O3-C refractories with Al, Si and SiO2 as the additives fired in the temperature range from 800 to 1400 掳C are investigated when multi-walled carbon nanotubes (MWCNTs) were used as the carbon source to partially or totally replace graphite flake in the materials. The results showed that the mechanical properties such as cold modulus of rupture (CMOR), modulus of elasticity (E) of all the specimens increased in the firing temperature range from 800 to 1200 掳C, but decreased dramatically at 1400 掳C. Compared with specimens with only graphite flake, specimens containing 0.05 wt%MWCNTs possessed better mechanical properties. However, they got deteriorated with the further increase of MWCNTs amount from 0.1 to 1 wt%. The differences in mechanical properties were closely associated with the microstructures of Al2O3-C refractories. In comparison with specimens having only graphite flake, the improvement of mechanical properties of specimens containing MWCNTs was attributed to strengthening and toughening mechanism of MWCNTs as well as formation of larger amount of ceramic phases in the matrix at 800 and 1000 掳C, respectively. At 1200 and 1400 掳C, the improvement was mainly associated with the quantity and morphology of SiC whiskers induced from MWCNTs in the specimens. However, with the increase of MWCNTs amount, the mechanical properties of the materials got deteriorated because of agglomeration of MWCNTs and their influence on the morphology of ceramics phases.