The longitudinal magnetoresistance of the Fe72Cu1V3Si16B8 melt spun ribbon in its as-cast and nanocrystalline state has been studied. Successive thermal treatments with increasing in current intensity from 33 to 43A/mm2 were applied for a fixed time (tan