Nanodomain formation and distribution in Gd-doped ceria

详细信息	查看全文 | 推荐本文 |

• 作者：Zhi-Peng Li^a ; ^b ; ^{zhipeng@email.unc.edu} ; Toshiyuki Mori^a ; Graeme John Auchterlonie^c ; Jin Zou^c ; ^d ; John Drennan^c
• 关键词：A. Nanostructures ; C. Electron Microscopy ; C. Electron diffraction ; D. Defects ; D. Microstructure
• 刊名：Materials Research Bulletin
• 出版年：2012
• 期刊代码：60_00255408
• 类别：ms
• 出版时间：March, 2012
• 卷：47
• 期：3
• 页码：763-767
• 文件大小：1054 K

摘要

A comprehensive study, with a combination of diverse analytical techniques, was performed to investigate nanodomain formation and distribution in gadolinium-doped ceria. It is illustrated that the nanodomain formation, originating from the aggregation and segregation of dopant cations together with associated charge-compensating oxygen vacancies, is ubiquitous throughout doped ceria. The formation of nanodomains is not limited to bulk areas as previously reported but exists at grain boundaries as well. With enhanced ordering level, such nanodomains formed at grain boundaries will decrease the ionic conductivity as a result of hindered the mobility of oxygen vacancies in doped ceria. Particularly, the nanodomains formed at grain boundaries, with strong defect interactions due to enrichment of dopants and ordered oxygen vacancies, are suggested to be another possible reason for the grain-boundary resistance, other than the widely accepted space-charge layers.