摘要
High temperature oxidation was performed on structural materials made of fibres of SiC in a SiC matrix (SiC/SiC) + 尾-SiC coating, considered for the cladding of the gas-cooled fast reactor. Tests carried out in various atmospheres (helium, nitrogen, air) coupled to mass variation, SEM and XPS analysis enabled the study of resistance to chemical degradation of such composites from 1400 to 2300 K. Monolithic 尾-SiC was also studied for comparison. The degradation of the composite material was faster than the monolithic one above 1970 K due to the damage of the 尾-SiC coating enabling the oxidizing species to penetrate inside the composite.