摘要
The phase relations in the Al–Dy–Ti ternary system at 500°C were investigated by powder X-ray diffraction (XRD), differential thermal analysis (DTA), optical microscopy and scanning electron microscopy (SEM) techniques. The existence of two ternary compounds DyTi2Al20 and Dy6Ti4Al43 were confirmed. The 500°C isothermal section of this ternary system consists of 14 single-phase regions, 27 two-phase regions and 14 three-phase regions. At 500°C, the maximum solid solubilities of Ti in Dy2Al, Dy3Al2 and DyAl2 is about 2.1at.%, 3.6at.%, 16.5at.%, respectively, and that of Dy in Ti, Ti3Al, TiAl is less than 1at.%.