摘要
In this study, the thermomechanical fatigue (TMF) and isothermal low-cycle-fatigue (LCF) behaviors of niobium-containing ferritic stainless steels are presented for the temperature range from 100 掳C to the maximum temperatures between 500 and 800 掳C; furthermore, we propose a new fatigue failure criterion to predict the fatigue lives of the components for different thermal cycle ranges using the TMF condition. Higher maximum temperatures during TMF cycle resulted in shorter TMF life. By modifying the Coffin-Manson equation using the temperature factor, we obtained a new parameter that was successfully correlated with the life under different maximum temperatures. The deformation responses during fatigue cycling and the fatigue microstructure were compared to elucidate the different fatigue behaviors under the TMF and LCF conditions.