A failure study of condenser tube manufactured from low nickel stainless steels
- 作者：D.N. Wasnik devendrawasnik@rediffmail.com
- 关键词：204 Stainless steel ; Grain pilling ; Intergranular corrosion ; Pitting corrosion ; Intergranular stress corrosion cracking
- 刊名：Engineering Failure Analysis
- 出版年：2012
- 期刊代码：53_13506307
- 类别：et
- 出版时间：July, 2012
- 卷：23
- 期：Complete
- 页码：69-75
- 文件大小：2050 K
摘要
A failure analysis of condenser tubes manufactured from Type 204 stainless steel was conducted to find the root cause of failures. The failures were observed in the parent materials of the tube rather than from welding or heat-affected zones. A detailed metallography, corrosion test and stress analysis study has been carried out to find out the root cause of failure, and it revealed that the parent materials of the tube were highly sensitized, and post-annealing treatment had been not performed by the manufacturers. The condenser tube failed prematurely due to sensitization and the presence of thermal residual stresses exacerbates this. This study emphasizes the metallurgical analysis performed to identify the root cause of failure of condenser tubes manufactured from Type 204 stainless steel.