In-pile electrochemical measurements on AISI 316 L(N) IG and EUROFER 97 – I: experimental results
- 作者：Vankeerberghen ; Marc ; Bosch ; Rik-Wouter ; Van Nieuwenhoven ; Rudi
- 关键词：C0400 ; N0100 ; S0600 ; S1000
- 刊名：Journal of Nuclear Materials
- 出版年：2003
- 期刊代码：51_00223115
- 类别：ms
- 出版时间：February, 2003
- 卷：312
- 期：2-3
- 页码：191-198
- 文件大小：674 K
摘要
In-pile electrochemical measurements were performed in order to investigate the effect of radiation on the electrochemical corrosion behaviour of two materials: reduced activation ferritic–martensitic steel EUROFER 97 and stainless steel AISI 316 L(N) IG. The corrosion potential was continuously monitored during the whole irradiation period. At regular intervals and under various flux levels, polarisation resistance measurements and electrochemical impedance spectroscopy were performed. Polarisation curves were recorded at the end of the reactor cycle. Analysis showed that the corrosion potential increased and the polarisation resistance decreased with the flux level. The impedance data showed two semi-circles in the Nyquist diagram which contracted with increasing flux level. A fit of the impedance data yielded a decrease of solution and polarisation resistances with the flux level. The polarisation curves could be fitted with a standard Butler–Volmer representation after correction for the solution resistance and showed an increase in the corrosion current density with the flux level.