摘要
Surface structure of Pt(3 1 0) = 3(1 0 0)x2013;(1 1 0), which contains kink atoms in the step, has been determined with the use of in situ surface X-ray scattering (SXS) in the double layer region (0.50 V(RHE)) in 0.1 M HClO4. Clean Pt(3 1 0) surface has pseudo (1 × 1) structure on which lateral displacements of 2x2013;9%and 0.3x2013;1%are found along a and b directions, respectively, whereas the surfaces of Pt(1 1 0) = 2(1 1 1)x2013;(1 1 1) and Pt(3 1 1) = 2(1 0 0)x2013;(1 1 1) are reconstructed to (1 × 2) according to previous reports. Interlayer spacing between the first and the second layers d12 is contracted about 5%compared with the bulk spacing, whereas those between underlying layers are expanded down to fourth layer. Fully adsorbed CO has no effect on the surface structure of Pt(3 1 0). This result differs from that on Pt(1 1 1), where d12 is expanded after CO adsorption.