摘要
A systematic investigation is performed on the dehydrogenation performance of TiB2-doped NaAlH4. A dramatic enhancement in the dehydrogenation kinetics of NaAlH4 is achieved by adding as-prepared TiB2 catalyst based on a low temperature solid phase reaction, whereas pure NaAlH4 exhibits a poor desorption kinetics. Thermodynamic analyses show that the onset dehydrogenation temperature of as-prepared TiB2-doped NaAlH4 is lowered to about 75聽掳C. In addition, the experimental results show that as-prepared TiB2-doped NaAlH4 after milling releases 3.60聽wt.%H2 for 1聽h and 5.21聽wt%H2 for 4聽h at 190聽掳C with a excellent dehydriding rate and capacity.