Sol–gel fabrication of compact, crack-free alumina film

详细信息	查看全文 | 推荐本文 |

• 作者：Chengbin Jing ; Xiujian Zhao ; Yongheng Zhang
• 关键词：A. Thin films ; B. Chemical synthesis ; B. Sol– ; gel chemistry ; D. Microstructure ; D. Surface properties
• 刊名：Materials Research Bulletin
• 出版年：2007
• 期刊代码：60_00255408
• 类别：ms
• 出版时间：12 April 2007
• 卷：42
• 期：4
• 页码：600-608
• 文件大小：572 K

摘要

Compact, crack-free alumina film was fabricated using an alumina sol with a high Al₂O₃ content. With the addition of ethylacetoacetate (CH₃COCH₂COOC₂H₅, EAcAc), the stable sol could be prepared with a molar ratio of aluminum sec-butoxide (Al(O-sec-Bu)₃, ASB) to water up to 1:25. It was found that EAcAc could notably decrease the surface tension of the liquid in the gel pores. The EAcAc modification layer on the colloidal particle retarded greatly the densification of the Al₂O₃ gel film and provided a long-lasting structural relaxation during heating. Therefore, the formation of cracks was effectively prevented in this alumina material. The alumina gel film contained a high Al₂O₃ content and there was a rather small mass loss during sintering. The critical thickness of Al₂O₃ sol–gel film was eight times higher than that could be achieved via the general sol–gel route and a film thicker than 0.8 μm was prepared by a single-step dipping operation.