摘要
For the first time, complex oxide NaFeYO7 + x was prepared by SHS (T c = 7508211;1200 K, U = 18211;4 mm/s) in the Na-Fe-Y-O system. Explored was the influence of reagents ratio on combustion limits for the mixtures under study. Combustion products were characterized by XRD, SEM, EDX, chemical analysis, and magnetic measurements. Single-phase NaFeYO7 + x was obtained at an excess of sodium in green mixtures. To stabilize the product, the water-washing procedure was used just after synthesis. The synthesized material has a cubic crystal structure with a cell parameter close to that of sodium yttrate NaYO2, it exhibited very weak magnetic properties, and overly-stoichiometric oxygen content. The product is heat resistant up to 450 K. The synthesized product is a new inorganic superoxide with good technological perspectives for use as a solid oxygen-containing material.