Influence of austenitizing temperature on apparent morphologies of as-quenched microstructures of steels
| 详细信息 | 推荐本文 | |
- 作者：Yue-jun Liu (12) liu_yue_jun@tom.com
Yi-min Li (2)
Bai-yun Huang (2) - 关键词：Key words martensite ; packet martensite ; plate martensite ; high temperature hardening
- 刊名：Journal of Central South University of Technology
- 出版时间：April 2006
- 出版年：2006
- 期刊代码：pc528_1005-9784
- 类别：et
- 卷：13
- 期：2
- 页码：122-129
- 数据来源：sp
摘要
The effects of austenitizing temperature on the morphologies and substructures of as-quenched microstructure were investigated by using 13 medium and high carbon steels. The formation reasons of various morphologies of martensite quenched at different austenitizing temperatures were also studied. The results show that the packet martensite in medium and high carbon steels quenched at higher austenitizing temperature is entirely different from that in as-quenched low carbon steels, which is still plate martensite, and not lath martensite. All the change laws of as-quenched microstructures in medium and high carbon steels are identical with an increase in austenitizing temperature, and the austenitizing temperature can merely change the combined morphology of martensitic platelets, but cannot alter the type of product of martensitic transformation in commercial steels.