Effect of manganese addition on hydrogen storage performance of vanadium-based BCC hydrogen storage alloys

详细信息

下载全文

推荐本文 |

• 作者：Chan-Yeol Seo (1)
  Zhao-Liang Zhang (1)
  Jin-Ho Kim (1)
  Paul S. Lee (1)
  Jai-Young Lee (1)
• 关键词：manganese ; vanadium ; based BCC alloys ; pressure ; composition (P− ; C) isotherms ; plateau pressure ; maximum and effective hydrogen storage capacities ; annealing heat ; treatment
• 刊名：Metals and Materials International
• 出版时间：July 2002
• 出版年：2002
• 期刊代码：pc365_1598-9623
• 类别：ch
• 卷：8
• 期：4
• 页码：341-346
• 数据来源：sp

摘要

The effect of manganese addition on hydrogen storage performance of vanadium-based BCC alloys was investigated by measuring mainly pressure-composition (P−C) isotherms at 303K. Annealing heat-treatment was also considered in selected cases. The XRD patterns showed BCC single phase in all the alloys. With increasing Mn content, the lattice parameters decreased linearly, thus resulting in an increase in plateau pressure and a reverse effect on maximum hydrogen storage capacity. However, an effective hydrogen storage capacity as high as 1.92 wt.%was achieved at x=0.075. V−Ti−Mn alloys showed a surprisingly flat desorption plateau, but lots of absorbed hydrogen cannot desorb at ambient temperature. Although V_0.44Ti_0.20Cr_0.12Mn_0.12Fe_0.12 alloy did not show the first plateau, both the maximum and effective hydrogen storage capacities were very low.