It is shown that upon cold rolling the deformation of an Fe-3%Si-0.5%Cu single crystal with a (110)[001] orientation occurs, along with slip, by twinning in the (112)[[`1][`1]1][\bar 1\bar 11] and (11[`2]\bar 2)[[`1][`1][`1]][\bar 1\bar 1\bar 1]. systems. Upon a reorientation of the crystal lattice due to the operation of the slip system (112)[[`1][`1]1][\bar 1\bar 11], the twins of the (112)[[`1][`1]1][\bar 1\bar 11] type occupy a regular position in the octahedral matrix (111)[[`1][`1]2][\bar 1\bar 12], retaining a special misorientation Σ3 with the matrix in the entire process of deformation. The twinning system (11[`2]\bar 2)[[`1][`1][`1]][\bar 1\bar 1\bar 1] occupies an irregular position in the (111)[[`1][`1]2][\bar 1\bar 12], matrix, but also proves to be in a special misorientation Σ3 with it. A dislocation mechanism is suggested, which makes it possible to explain the retention of the special misorientation and the inclination of the habit plane of twins of both systems of twins.