摘要
通过拉伸、硬度、冲击试验研究了时效温度、时间对2507超级双相不锈钢力学性能的影响,并应用EBSD技术观察了σ相的析出。结果表明:在900~1000℃区域,随时效温度降低,σ相析出量增加,材料塑性变差,温度低于940℃时效10 min其伸长率低于10%;在600~700℃区域,随时效温度升高,σ相析出量增加,但析出时间较高温区域长,力学性能恶化不太严重,600~650℃时效40 h内伸长率>20%,冲击吸收能量>10 J。
Effects of aging temperature and time on mechanical properties of 2507 super duplex stainless steel were studied by means of tensile,hardness and impact tests,and the precipitation of the σ phase was observed by means of EBSD. The results show that with the decrease of aging temperature,the precipitation of the σ-phase increases and the plasticity of the material becomes worse at 900-1000 ℃region,the elongation is lower than 10% under the condition of aging temperature below 940 ℃ and aged for 10 min. At 600-700 ℃ region,with the increase of aging temperature,the precipitation of the σ-phase increases,but the aging time is greatly prolonged compared with that the higher temperature region,and the deterioration of mechanical properties is not very serious,the elongation is higher than 20% and impact absorbed energy is higher than 10 J under the aging condition of 600-650 ℃ and 40 h.
引文
[1]肖纪美.不锈钢的金属学问题[M].北京:冶金工业出版社,1983.
[2]陈兴润,潘吉祥.固溶温度对2205双相不锈钢组织和点蚀性能的影响[J].金属热处理,2014,39(12):38-42.Chen Xingrun,Pan Jixiang.Influence of solution temperature on microstructure and pitting corrosion of 2205 duplex stainless steel[J].Heat Treatment of Metals,2014,39(12):38-42.
[3]孙祺,王剑,何燕,等.时效时间对2205双相不锈钢中第二相析出行为的影响[J].金属热处理,2016,41(2):63-66.Sun Qi,Wang Jian,He Yan,et al.Influence of aging time on precipitation behavior of 2205 duplex stainless steel[J].Heat Treatment of Metals,2016,41(12):63-66.
[4]黄澳,陈吉,宋见,等.时效时间对2205双相不锈钢组织与疲劳裂纹扩展规律的影响[J].金属热处理,2016,41(10):167-171.Huang Ao,Chen Ji,Song Jian,et al.Effect of aging time on microstructure and fatigue crack propagation behavior of 2205 duplex stainless steel[J].Heat Treatment of Metals,2016,41(10):167-171.
[5]黄锐.S31803双相不锈中σ析出相及其对性能的影响研究[D].西安:西安建筑科技大学,2009.
[6]吴玖.双相不锈钢[M].北京:冶金工业出版社,1999.