摘要
主要从三类玻纤增强聚丙烯材料PP-GF20、PP-GF35、PP-GF50进行研究,通过研究聚丙烯基体、相容剂与玻纤种类对玻纤增强聚丙烯性能的影响,对配方进行特定的优化,使材料的力学性能有显著提高,GFPP-20的拉伸强度可达86 MPa、弯曲强度可达118 MPa,GFPP-35的拉伸强度可达114 MPa、弯曲强度可达158 MPa,GFPP-50的拉伸强度可达123 MPa、弯曲强度可达167 MPa。
The article studied three kind of glass fiber( GF) filled polypropylene( PP) composites including PP-GF20,PP-GF35 and PP-GF50. The effect of PP resin,PP graft maleic anhydride( PP-gMAH) and glass fiber on the properties of short glass fiber filled PP composites was also researched. The results show that the specific optimization of the formulation makes the mechanical properties of the material significantly improved as follows: the highest tensile and flexural strengths of PP-GF20,PP-GF35 and PPGF50 achieve 86 MPa/118 MPa,114 MPa/158 MPa,and 123 MPa/167 MPa,respectively.
引文
[1]胡友良.聚烯烃功能化及改性[M].北京:化学工业出版社,2008.
[2]王经.塑料改性技术[M].北京:化学工业出版社,2004.
[3]邵静波. PP-g-MAH对玻璃纤维增强PP的影响[J].合成树脂及塑料,2006,23(4):5-8.
[4]洪定一.聚丙烯-原理、工艺与技术[M].北京:中国石化出版社,2007.
[5]李正光.聚丙烯生产技术及应用[M].北京:石油工业出版社,2006.
[6]周殿明,张丽珍.聚丙烯成型技术问答[M].北京:化学工业出版社,2007.
[7]张超.长玻璃纤维增强聚丙烯复合材料力学性能研究[J].塑料工业,2017,45(12):78-82.
[8]张超.长玻纤增强PP/PA6合金材料的性能[J].工程塑料应用,2017,45(11):7-12.
[9]韩领. GF增强PP复合材料的尺寸稳定性与力学性能[J].工程塑料应用,2017,45(5):24-28.
[10]唐梓健.聚丙烯/玻璃纤维/滑石粉复合材料的制备及性能研究[J].塑料工业,2017,45(1):80-83.
[11]张伟.低气味低VOC玻纤增强聚丙烯材料的研制[J].工程塑料应用,2017,45(1):35-38.
[12]黎敏荣.纤维增强热塑性树脂复合材料成型技术研究进展[J].塑料工业,2016,44(11):5-10.