改善含硼尾矿活性的研究
|
摘要
含硼尾矿是铁硼镁矿选铁后所遗留的尾矿,对其中硼元素的回收是目前亟待解决的问题,而硼的回收要求尾矿具有很高的活性。采用焙烧和添加钙化剂的方法改善含硼尾矿的硼活性,研究了焙烧温度、焙烧时间以及添加剂加入量对活性的影响。结果表明,当焙烧温度为700℃、焙烧时间为2 h、添加剂质量分数为21.5%时,硼尾矿活性可达91%左右。
The boron bearing tailing is a kind of tailing which is remainde after the enrichment of iron from iron boron magnesium ore, and the recycling of boron element is a problem to be solved currently, and the high boron-activity of tailing is also necessary. The boron-activity of boron-containing tailing was improved by calcination with the addition of calcification agent, and the effects of calcination temperature, calcination time and the dosage of additive on the activity were investigated. The results showed that when the calcination temperature was 700 ℃, the calcination time was 2 h, and the mass fraction of additive was 21.5%, the activity of boron-containing tailing could reach about 91%.
The boron bearing tailing is a kind of tailing which is remainde after the enrichment of iron from iron boron magnesium ore, and the recycling of boron element is a problem to be solved currently, and the high boron-activity of tailing is also necessary. The boron-activity of boron-containing tailing was improved by calcination with the addition of calcification agent, and the effects of calcination temperature, calcination time and the dosage of additive on the activity were investigated. The results showed that when the calcination temperature was 700 ℃, the calcination time was 2 h, and the mass fraction of additive was 21.5%, the activity of boron-containing tailing could reach about 91%.
引文
[1]唐尧,陈春琳,熊先孝,等.世界硼资源分布及开发利用现状分析[J].现代化工,2013,33(10):1-4,6.
[2]郑学家.硼化合物生产与应用[M].2版.北京:化学工业出版社,2014:27-37.
[3]宋丽.富硼渣常压碱浸及浸出液净化结晶硼砂的研究[D].沈阳:东北大学,2013.
[4]郎建峰,李炳焕,曹文华.富硼渣的碱解反应及活性评价方法的研究.河北化工,1997(2):16-17.
[5]李炳焕,曹文华.碱解法从硼铁矿中提取硼的研究.化学工程师,2002(2):13,15.
[6]王明玉,王学文.石煤提钒浸出过程研究现状与展望[J].稀有金属,2010,34(1):90-97.
[7]何丹,仲剑初,王洪志,等.富硼渣钙化焙烧研究[J].化工矿物与加工,2010(6):13-16.
[8]天津化工研究院.无机盐工业手册[M].2版.北京:化学工业出版社,1996.
[9]李晓军,张润平,谢兵.钒渣钙化焙烧参数对钒浸出率的影响[J].过程工程学报,2012,12(1):54-58.
[10]郎建峰,曹文华.高炉铁硼分离富硼渣活性的研究[J].无机盐工业,1994(4):4-6.
[2]郑学家.硼化合物生产与应用[M].2版.北京:化学工业出版社,2014:27-37.
[3]宋丽.富硼渣常压碱浸及浸出液净化结晶硼砂的研究[D].沈阳:东北大学,2013.
[4]郎建峰,李炳焕,曹文华.富硼渣的碱解反应及活性评价方法的研究.河北化工,1997(2):16-17.
[5]李炳焕,曹文华.碱解法从硼铁矿中提取硼的研究.化学工程师,2002(2):13,15.
[6]王明玉,王学文.石煤提钒浸出过程研究现状与展望[J].稀有金属,2010,34(1):90-97.
[7]何丹,仲剑初,王洪志,等.富硼渣钙化焙烧研究[J].化工矿物与加工,2010(6):13-16.
[8]天津化工研究院.无机盐工业手册[M].2版.北京:化学工业出版社,1996.
[9]李晓军,张润平,谢兵.钒渣钙化焙烧参数对钒浸出率的影响[J].过程工程学报,2012,12(1):54-58.
[10]郎建峰,曹文华.高炉铁硼分离富硼渣活性的研究[J].无机盐工业,1994(4):4-6.