摘要
对H型秸秆混凝土砌块构成的有芯柱的自保温暗骨架承重墙和无芯柱同型砌块构成的墙体进行了保温性能和抗压强度对比试验。结果表明:有芯柱的自保温暗骨架承重墙传热系数为0.65 W/(m~2·K),无芯柱的对照墙体传热系数为0.54 W/(m~2·K),有芯柱墙体比无芯柱墙体的传热系数增大了20.4%;有芯柱自保温暗骨架承重墙的抗压强度为10.59 MPa,比无芯柱试验墙的抗压强度(6.26 MPa)提高了69.2%。芯柱的引入显著提高了自保温砌体的抗压强度,但降低了其保温性能。
Experimental research on thermal insulation performance and compressive strength of self-insulating structural wall with inner frame consists of H-type straw concrete block. Comparing experiment of the wall constructed by the same wall without core column also had been carried out. The results show that heat transfer coefficient of the wall with core column was 0.65 W/(m~2·K),which was 20.4 percent higher than the wall without core column with the value of 0.54 W/(m~2·K). Compressive strength of the wall with core column was 10.59 MPa,which was 69.2 percent larger than the wall without core column with compression strength 6.26 MPa. Self-insulating structural wall with inner frame had better compressive strength but had lower heat in-sulating performance by comparing with the wall without inner frame.
引文
[1]方放,李想,石祖梁,等.黄淮海地区农作物秸秆资源分布及利用结构分析[J].农业工程学报,2015,31(2):228-234.
[2]周涛,王少杰,刘福胜,等.混凝土夹心秸秆块砌块砌体偏心受压承载力试验研究[J].建筑科学,2017,33(9):66-70.
[3]侯少丹,王少杰,刘福胜,等.H型混凝土夹芯秸秆砌块墙热湿耦合传递特性研究[J].新型建筑材料,2017(2):62-65.
[4]吴聪,刘福胜,范军,等.工字型自保温混凝土夹心秸秆砌块墙体热工性能研究[J].混凝土,2015(6):127-130.
[5]侯少丹,张慧瑾,刘福胜,等.夹芯秸秆混凝土砌块试点建筑保温节能性能研究[J].新型建筑材料,2017(3):56-59.
[6]范军,王宏斌,刘福胜,等.小麦秸秆压缩块吸放湿性能实验研究[J].新型建筑材料,2013(8):48-50.
[7]孙雷.自保温暗骨架承重墙结构抗震性能研究[D].泰安:山东农业大学,2014.
[8]武义馨.自保温暗骨架承重墙抗剪性能试验研究与分析[D].泰安:山东农业大学,2016.