摘要
通过与外养护技术的对比,研究了内养护技术对混凝土强度、电通量及收缩的影响,结果表明温度对混凝土强度、耐久性能有影响,温度低不利于混凝土强度发展与耐久性提高,适宜的养护温度为20℃以上。针对混凝土强度的发展,内养护技术优于外养护剂养护,相比于养护膜养护和土工布包裹洒水养护效果稍差,采用SAP内养护对提高混凝土密实性没有优势。
Compared with external curing,this study focused on internal curing and its impact on the intensity,electric flux and shrinkage of concrete.The results show that temperature is a key factor to concrete intensity and durability,low temperature is detrimental to its intensity development and durability maintenance.Therefore,20 ℃ or above can be appropriate for the curing process.Moreover,internal curing is effective to improve concrete intensity when compared with external compound curing,but less effective when compared with membrane curing or geotextile/watering curing.In addition,the study proves that SAP internal curing shows no advantage on improving concrete intensity.
引文
[1]马丽媛.高强混凝土收缩开裂的研究[D].北京:中国建筑材料科学研究院,2001.
[2]冷发光、王永海、周永祥,等.高强混凝土的研究应用和发展趋势[J].商品混凝土,2011(1):25-29.
[3]查进.超大跨径混合梁斜拉桥宽箱梁高性能混凝土防裂技术与耐久性研究[D].武汉:武汉理工大学,2008.
[4]谢伟峰、李丽娟、陈智泽等.高强混凝土高温下爆裂机理探讨[J].新型建筑材料,2007(1):70-72.
[5]董汇标,胡钊光,夏京亮,等.养护方式对天然火山灰高性能混凝土性能的影响[J].混凝土,2016(5):135-138.
[6]马先伟、张家科、刘剑辉.高性能水泥基材料内养护剂用高吸水树脂的研究进展[J].硅酸盐学报,2015(8):1099-1110.
[7]朱长华、李享涛、王保江,等.内养护对混凝土抗裂性及水化的影响[J].建筑材料学报,2013,16(2):221-225.
[8]陈德鹏,钱春香,高桂波,等.高吸水树脂对混凝土收缩开裂的改善作用及其机理[J].功能材料,2007,38(3):475-478.
[9]张子明、周红军、赵吉坤.温度对混凝土强度的影响[J].河海大学学报,2004(6):674-679.
[10]胡曙光,周宇飞,王发洲,等.高吸水性树脂颗粒对混凝土自收缩与强度的影响[J].华中科技大学学报,2008(3):1.