TiAlN涂层高温行为的研究进展
|
摘要
综述了关于TiAlN涂层的高温结构转变、高温氧化行为及机理、高温磨损行为、高温力学性能、高温腐蚀行为等方面的研究进展,为TiAlN涂层的技术开发提供一定的理论基础。
The research progress of TiAlN coatings in respect of structural transformation, oxidation behavior and mechanism, wear behavior, mechanical properties, and corrosion behavior at high temperatures was reviewed, providing a theoretical basis for the development of TiAlN coating technology.
The research progress of TiAlN coatings in respect of structural transformation, oxidation behavior and mechanism, wear behavior, mechanical properties, and corrosion behavior at high temperatures was reviewed, providing a theoretical basis for the development of TiAlN coating technology.
引文
[1] KOLLER C M,HOLLERWEGER R, SABITZER C, et al. Thermal stability and oxidation resistance of arc evaporated TiAlN, TaAlN, TiAlTaN, and TiAlN/TaAlN coatings[J]. Surface and Coatings Technology, 2014, 259:599-607.
[2]张克栋.基体表面织构化TiAlN涂层刀具的制备与应用的基础研究[D].济南:山东大学,2017.
[3]周军,樊湘芳,丰振东,等.Zr4合金表面多弧离子镀TiAlSiN涂层的微观形貌与性能[J].粉末冶金材料科学与工程,2017,22(5):687-692.
[4]彭笑,朱丽慧,KUMAR V,等.PVD制备TiAlSiN涂层的研究进展[J].材料导报,2014, 28(3):42-44,74.
[5]金犁.多弧离子镀制备Ti_(1-x)Al_xN薄膜的工艺及其性能研究[D].武汉:武汉科技大学,2006.
[6]胡志杰,李争显,王宝云,等.工艺参数对Ti合金表面电弧离子镀TiA1N涂层的性能影响[J].热加工工艺,2008,37(12):109-112.
[7]毛延发,宫永辉,杨琳,等.多弧离子镀TiAlN涂层熔滴工艺参数的影响[J].内蒙古民族大学学报(自然科学版),2007,22(5):514-517.
[8]徐培利.TiAlN刀具涂层的微喷砂加工表面完整性研究[D].济南:山东大学,2016.
[9]张雨萌,朱丽慧,倪旺阳,等.Al含量对TiAlN涂层热稳定性能的影响[J].中南大学学报(自然科学版),2013,44(7):2696-2701.
[10]王永康,熊仁章,雷廷权,等.Ti_(1-x)Al_xN涂层的组织结构及Al元素的作用机理[J].宁波大学学报(理工版),2001,14(4):48-51.
[11]陈利.Ti-Al-N基硬质涂层的热稳定性能、微结构及其力学、切削性能的研究[D].长沙:中南大学,2009.
[12] HORLING A, HULTMAN L, ODEN M, et al. Thermal stability of arc evaporated high aluminum-content Ti_(1-x)Al_xN thin films[J]. Journal of Vacuum Science&Technology A:Vacuum, Surfaces, and Films, 2002, 20(5):1815-1823.
[13]赵升升,周晟昊,曾德长.退火对大厚度TiA1N涂层力学性能影响的研究[J].真空科学与技术学报,2017, 37(2):182-187.
[14] XU Y X, CHEN L, PEI F, et al. Influence of Hf on the structure, thermal stability and oxidation resistance of Ti-Al-N coatings[J]. Thin Solid Films, 2014,565:25-31.
[15]潘晓龙,王少鹏,李争显,等.钛合金表面电弧离子镀TiA1N涂层的耐高温性能[J].稀有金属材料与工程,2008,37(增刊4):598-601.
[16]冯长杰,陈恩.电弧离子镀TiA1N、TiA1SiN涂层在高温及变温环境中的摩擦学性能[J].中国表面工程,2017, 30(5):17-27.
[17]潘晓龙,王少鹏,李争显,等.电弧离子镀TiA1N涂层的热疲劳及抗氧化性能[J].真空科学与技术学报,2008(增刊):60-63.
[18]张馨元,赵广彬,孙爱祥,等.非平衡磁控溅射TiAlN薄膜的高温抗氧化性能研究[J].真空,2011, 48(5):61-63.
[19] ZHU L H, HU M M, NI W Y, et al. High temperature oxidation behavior of Ti_(0.5)Al_(0.5)N coating and Ti_(0.5)Al_(0.4)Si_(0.1)N coating[J]. Vacuum, 2012, 86(12):1795-1799.
[20]彭红瑞,石玉龙,谢广文,等.用PCVD法制备抗高温氧化涂层的研究[J].青岛化工学院学报,1999, 20(3):245-247.
[21]张贝贝,张程煜,折洁,等.磁控溅射TiAlN涂层抗氧化性能的研究进展[J].材料导报,2013, 27(21):14-18.
[22]张勇.TiAlN硬质薄膜抗氧化性能研究[D].成都:西华大学,2010.
[23]杜日昇.高Al含量Ti-Al-N系硬质涂层的制备及其抗氧化性能的研究[D].广州:华南理工大学,2011.
[24]杨鸿泰,代明江,李洪,等.Al含量对TiAlN涂层组织结构和性能的影响[J].材料导报,2018, 32(20):3573-3578, 3589.
[25]冯长杰,辛丽,李明升,等.电弧离子镀梯度(Ti,Al)N薄膜的结构与抗氧化性能[J].中国腐蚀与防腐学报,2008,28(1):1-6.
[26]王永康,雷廷权,夏立芳,等.Ti_(0.5)Al_(0.5)N涂层的抗高温氧化行为[J].材料工程,2001(1):12-14.
[27]汝强,胡社军,黄拿灿,等.钛合金表面电弧离子镀TiA1N涂层的抗高温氧化性能研究[J].材料保护,2007,40(1):28-31.
[28] SHIAO M H, SHIEU F S. A formation mechanism for the macroparticles in arc ion-plated TiN films[J]. Thin Solid Films, 2001, 386(1):27-31
[29] ZHOU M, MAKINO Y, NOSE M, et al. Phase transition and properties of Ti-Al-N thin films prepared by r.f,-plasma assisted magnetron sputtering[J]. Thin Solid Films, 1999, 339(1/2):203-208
[30] LUGSCHEIDER E, KNOTEK O, LOFFLER F, et al. Deposition of arc TiA1N coatings with pulsed bias[J]. Surface and Coatings Technology, 1995, 76/77(Part 2):700-705.
[31]刘爱华.PVD氮化物涂层的高温摩擦磨损特性及机理研究[D].济南:山东大学,2012.
[32]曾琨,邹长伟,郑军,等.电弧离子镀TiA1N和TiA1SiN涂层的高温摩擦磨损行为[J].中国表面工程,2015, 28(6):28-38.
[33]牛秋林,陈云,杨军.MDT涂层高温滑动摩擦特性试验研究[J].工具技术,2017,51(10):24-26.
[34]吴娜梅.几种氮化物涂层高温磨损性能研究[D].南昌:南昌航空大学,2015.
[35]王新.炮钢表面磁控溅射制备TiA1VN膜层及性能的研究[D].沈阳:沈阳工业大学,2017.
[36] ZHANG M M,XIN L, DING X Y, et al. Effects Ti/TiA1N composite multilayer coatings on corrosion resistance of titanium alloy in solid NaCl-H_2O-O_2 at600℃[J].Journal of Alloys and Compounds, 2018,734:307-317.
[2]张克栋.基体表面织构化TiAlN涂层刀具的制备与应用的基础研究[D].济南:山东大学,2017.
[3]周军,樊湘芳,丰振东,等.Zr4合金表面多弧离子镀TiAlSiN涂层的微观形貌与性能[J].粉末冶金材料科学与工程,2017,22(5):687-692.
[4]彭笑,朱丽慧,KUMAR V,等.PVD制备TiAlSiN涂层的研究进展[J].材料导报,2014, 28(3):42-44,74.
[5]金犁.多弧离子镀制备Ti_(1-x)Al_xN薄膜的工艺及其性能研究[D].武汉:武汉科技大学,2006.
[6]胡志杰,李争显,王宝云,等.工艺参数对Ti合金表面电弧离子镀TiA1N涂层的性能影响[J].热加工工艺,2008,37(12):109-112.
[7]毛延发,宫永辉,杨琳,等.多弧离子镀TiAlN涂层熔滴工艺参数的影响[J].内蒙古民族大学学报(自然科学版),2007,22(5):514-517.
[8]徐培利.TiAlN刀具涂层的微喷砂加工表面完整性研究[D].济南:山东大学,2016.
[9]张雨萌,朱丽慧,倪旺阳,等.Al含量对TiAlN涂层热稳定性能的影响[J].中南大学学报(自然科学版),2013,44(7):2696-2701.
[10]王永康,熊仁章,雷廷权,等.Ti_(1-x)Al_xN涂层的组织结构及Al元素的作用机理[J].宁波大学学报(理工版),2001,14(4):48-51.
[11]陈利.Ti-Al-N基硬质涂层的热稳定性能、微结构及其力学、切削性能的研究[D].长沙:中南大学,2009.
[12] HORLING A, HULTMAN L, ODEN M, et al. Thermal stability of arc evaporated high aluminum-content Ti_(1-x)Al_xN thin films[J]. Journal of Vacuum Science&Technology A:Vacuum, Surfaces, and Films, 2002, 20(5):1815-1823.
[13]赵升升,周晟昊,曾德长.退火对大厚度TiA1N涂层力学性能影响的研究[J].真空科学与技术学报,2017, 37(2):182-187.
[14] XU Y X, CHEN L, PEI F, et al. Influence of Hf on the structure, thermal stability and oxidation resistance of Ti-Al-N coatings[J]. Thin Solid Films, 2014,565:25-31.
[15]潘晓龙,王少鹏,李争显,等.钛合金表面电弧离子镀TiA1N涂层的耐高温性能[J].稀有金属材料与工程,2008,37(增刊4):598-601.
[16]冯长杰,陈恩.电弧离子镀TiA1N、TiA1SiN涂层在高温及变温环境中的摩擦学性能[J].中国表面工程,2017, 30(5):17-27.
[17]潘晓龙,王少鹏,李争显,等.电弧离子镀TiA1N涂层的热疲劳及抗氧化性能[J].真空科学与技术学报,2008(增刊):60-63.
[18]张馨元,赵广彬,孙爱祥,等.非平衡磁控溅射TiAlN薄膜的高温抗氧化性能研究[J].真空,2011, 48(5):61-63.
[19] ZHU L H, HU M M, NI W Y, et al. High temperature oxidation behavior of Ti_(0.5)Al_(0.5)N coating and Ti_(0.5)Al_(0.4)Si_(0.1)N coating[J]. Vacuum, 2012, 86(12):1795-1799.
[20]彭红瑞,石玉龙,谢广文,等.用PCVD法制备抗高温氧化涂层的研究[J].青岛化工学院学报,1999, 20(3):245-247.
[21]张贝贝,张程煜,折洁,等.磁控溅射TiAlN涂层抗氧化性能的研究进展[J].材料导报,2013, 27(21):14-18.
[22]张勇.TiAlN硬质薄膜抗氧化性能研究[D].成都:西华大学,2010.
[23]杜日昇.高Al含量Ti-Al-N系硬质涂层的制备及其抗氧化性能的研究[D].广州:华南理工大学,2011.
[24]杨鸿泰,代明江,李洪,等.Al含量对TiAlN涂层组织结构和性能的影响[J].材料导报,2018, 32(20):3573-3578, 3589.
[25]冯长杰,辛丽,李明升,等.电弧离子镀梯度(Ti,Al)N薄膜的结构与抗氧化性能[J].中国腐蚀与防腐学报,2008,28(1):1-6.
[26]王永康,雷廷权,夏立芳,等.Ti_(0.5)Al_(0.5)N涂层的抗高温氧化行为[J].材料工程,2001(1):12-14.
[27]汝强,胡社军,黄拿灿,等.钛合金表面电弧离子镀TiA1N涂层的抗高温氧化性能研究[J].材料保护,2007,40(1):28-31.
[28] SHIAO M H, SHIEU F S. A formation mechanism for the macroparticles in arc ion-plated TiN films[J]. Thin Solid Films, 2001, 386(1):27-31
[29] ZHOU M, MAKINO Y, NOSE M, et al. Phase transition and properties of Ti-Al-N thin films prepared by r.f,-plasma assisted magnetron sputtering[J]. Thin Solid Films, 1999, 339(1/2):203-208
[30] LUGSCHEIDER E, KNOTEK O, LOFFLER F, et al. Deposition of arc TiA1N coatings with pulsed bias[J]. Surface and Coatings Technology, 1995, 76/77(Part 2):700-705.
[31]刘爱华.PVD氮化物涂层的高温摩擦磨损特性及机理研究[D].济南:山东大学,2012.
[32]曾琨,邹长伟,郑军,等.电弧离子镀TiA1N和TiA1SiN涂层的高温摩擦磨损行为[J].中国表面工程,2015, 28(6):28-38.
[33]牛秋林,陈云,杨军.MDT涂层高温滑动摩擦特性试验研究[J].工具技术,2017,51(10):24-26.
[34]吴娜梅.几种氮化物涂层高温磨损性能研究[D].南昌:南昌航空大学,2015.
[35]王新.炮钢表面磁控溅射制备TiA1VN膜层及性能的研究[D].沈阳:沈阳工业大学,2017.
[36] ZHANG M M,XIN L, DING X Y, et al. Effects Ti/TiA1N composite multilayer coatings on corrosion resistance of titanium alloy in solid NaCl-H_2O-O_2 at600℃[J].Journal of Alloys and Compounds, 2018,734:307-317.