摘要
利用OM、SEM和EDS研究了定向凝固速度对Cu-2. 5%Cr合金中带状组织形貌和成分偏析的影响,并对不同形态的带状组织的形成机制进行了分析。结果表明:在5~50μm/s的定向凝固速率下,Cu-2. 5%Cr合金会产生平界面与共晶、胞状组织与共晶、柱状树枝晶与共晶三种不同形态的带状组织。这是由于凝固速率达到了平/胞转换临界速率以及胞/枝转换临界速率。带状组织的形成伴随着大量的溶质扩散与偏析,随着定向凝固速率的增大,带状组织中成分偏析增大,且带状组织愈加清晰。
The impact of directional solidification rate on the morphology and composition segregation of band-like structures in Cu-2. 5% Cr alloy were investigated by means of OM,SEM and EDS. The formation mechanism of band-like structures with diverse morphology was analyzed as well. The results showed that three different forms of band-like structures including: flat interface and eutectic,cell structure and eutectic,columnar dendrites and eutectic would be generated in the Cu-2. 5% Cr alloy,at the directional solidification rates of 5—50 m/s. This was because the solidification rate reached the critical rate of flat/cell transition and the critical rate of cell/branch transition. The formation of band-like structure was accompanied by a large amount of solute diffusion and segregation. With the increase of directional solidification rate,the segregation of band-structure was enhanced,and the band-like structure became more distinct.
引文
1 Weatherly G C,Humble P,Borland D.Acta Metallurgica,1979,27(12),1817.
2 Batra I S,Dey G K,Kulkarni U D,et al.Journal of Nuclear Materials,2001,299(2),95.
3 Hall M G,Aaronson H I,Kinsma K R.Surface Science,1972,31(72),265.
4 Liu J L,Ruan F,Wang E D,et al.Materials Review,2005,19(7),8(in Chinese).刘京雷,阮锋,王尔德,等.材料导报,2005,19(7),8.
5李琨,苏彦庆,骆良顺,等.中国机械工程学会第十二届铸造年会.广州,2011,195.
6 Dobler S,Lo T S,Plapp M,et al.Acta Materialia,2004,52(9),2798.
7 Su Yanqing,Luo Liangshun,Li Xinzhong,et al.Applied Physics Letters,2006,89(23),272.
8 Luo L S,Zhang Y M,Su Y Q,et al.Acta Metallurgica Sinica,2011,47(3),278(in Chinese).骆良顺,张宇民,苏彦庆,等.金属学报,2011,47(3),278.
9 Zhang J F,Shen J,Shang Z,et al.Rare Metal Materrials And Engineering,2013,42(2),265(in Chinese).张建飞,沈军,商昭,等.稀有金属材料与工程,2013,42(2),265.
10 Li X L,Li J S,Tang L,et al.Rare Metal Materrials and Engineering,2008,37(4),615(in Chinese).李晓历,李金山,唐玲,等.稀有金属材料与工程,2008,37(4),615.
11 Bi X Q,Hu R,Li J S,et al.Material Science and Technology,2005,13(2),153(in Chinese).毕晓勤,胡锐,李金山,等.材料科学与工艺,2005,13(2),153.
12 Li Y,Zhu J,Wang Y,et al.Materials Review B:Research Papers,2018,32(2),602(in Chinese).李勇,朱靖,王莹,等.材料导报:研究篇,2018,32(2),602.
13 Bi X Q,Fu H Z,Hu R,et al.Transactions of Metal Heat Treatment,2007,32(8),38(in Chinese).毕晓勤,傅恒志,胡锐,等.金属热处理,2007,32(8),38.
14 Tang L,Li S M,Ai T T,et al.Materials for Mechanical Engineering,2010,34(4),33(in Chinese).唐玲,李双明,艾桃桃,等.机械工程材料,2010,34(4),33.
15 Li Y S,Zhai H,Wang T,et al.Foundry,2008,57(3),220(in Chinese).李玉胜,翟虎,王涛,等.铸造,2008,57(3),220.
16 Zhong H,Li S M,Liu L,et al.Materials Review,2006,20(9),100(in Chinese).钟宏,李双明,刘林,等.材料导报,2006,20(9),100.
17 Li X L,Microstructure evolution of directionally solidified Cu-Cr alloy.Ph.D.Thesis,Northwestern Polytechnical University,China,2006(in Chinese).李晓历.Cu-Cr合金定向凝固组织演化研究.博士毕业论文,西北工业大学,2006.
18 Huang W D,Ding G L,Zhou Y H,et al.Chinese Jounal of Materials Research,1995,9(3),201(in Chinese).黄卫东,丁国陆,周尧和,等.材料研究学报,1995,9(3),201.
19 Li X L,Li J S,Hu R,et al.Acta Metallurgica Sinica,2007,43(12),1258(in Chinese).李晓历,李金山,胡锐,等.金属学报,2007,43(12),1258.
20 Luo L S,Fu H Z,Zhang Y M,et al.Acta Metallurgica Sinica,2011,47(3),288(in Chinese).骆良顺,傅恒志,张宇民,等.金属学报,2011,47(3),288.
21 Kurz W,Fisher D J.Acta Metallurgica,1981,29(1),16.
22 Liu T,Luo L S,Zhang Y N,et al.Acta Metallurgica Sinica,2016,52(7),870(in Chinese).刘桐,骆良顺,张延宁,等.金属学报,2016,52(7),870.
23 Ge B M,Liu Lin,Zhang S X,et al.Acta Metallurgica Sinica,2011,47(11),1473(in Chinese).葛丙明,刘林,张胜霞,等.金属学报,2011,47(11),1473.
24 Zhang Y.Microstructure evolution of directionally solidified Cu-20wt%Sn peritectic alloy.Ph.D.Thesis,Harbin Institute of Technology,China,2010(in Chinese).张元.Cu-20wt%Sn包晶合金定向凝固组织演化规律.博士学位论文,哈尔滨工业大学,2010.
25 Jiang L W,Li S S,Qiu Z C,et al.Acta Metallurgica Sinica,2009,45(5),550(in Chinese).蒋立武,李树索,邱自成,等.金属学报,2009,45(5),550.
26 Wu Y,Pan F S,Jiang B,et al.Journal of Materials Engineering,2011(4),71(in Chinese).吴裕,潘复生,蒋斌,等.材料工程,2011(4),71.