基于2196-T8511铝锂合金,对其进行重固溶-再时效处理,研究时效时间对其力学性能与组织演化的影响。结果表明:重固溶处理后的晶界清晰。再采用适当的温度和时间进行时效处理,合金可以回复到原始态的力学性能。2196铝锂合金的重新固溶-再时效析出相包括T1相(Al_2Cu Li)、δ'相(Al_3Li)和θ'相(Al_2Cu);较短时效时间可形成较多δ'相和θ'相。随着时效时间的延长,T1相逐渐增多,δ'相和θ'相减少;重新固溶-时效后,断口韧窝增加,仍以分层断裂为主。
Based on 2196-T8511 Al-Li alloy, the effects of aging time on the mechanical properties and microstructure evolution during re-aging and re-solution were investigated. The results show that, the grain boundary after re-solution is clear.The mechanical properties can recover to the original state by using appropriate re-aging temperature and time. The intragranular precipitates include T1(Al_2 Cu Li), δ'(Al_3 Li) and θ'(Al_2 Cu). Re-aging for shorter time, more δ' and θ' precipitates are formed. With the aging time increaing, T1 precipitates increase, but θ' and δ' precipitates decrease. After re-solution and aging, the dimples of fracture increase and delamination fracture is dominant.
引文
[1]王浩军,史春玲,杨文华,等.时效时间对2198铝锂合金组织和力学性能的影响[J].热加工工艺,2013,42(8):187-189.
[2]乔勇,冯朝辉,柴丽华,等.固溶处理对新型铝锂合金X2A66组织和性能的影响[J].热加工工艺,2017,46(2):208-211.
[3]付小强,马超,鲍鹏里,等.时效处理对新型铝锂合金组织及力学性能的影响[J].金属热处理,2014,39(5):70-73.
[4]尚勇,李建康,张立武.重固溶再时效处理对7175铝合金组织和性能的影响[J].热加工工艺,2005,34(5):35-38.
[5]尚勇,张立武,李建康.重固溶再多级时效处理对7175铝合金组织和性能的影响[J].热加工工艺,2005,34(7):41-43.
[6]马云龙,李劲风,刘观日,等.重固溶-不同温度T8再时效2195铝锂合金的力学性能与显微组织演化[J].中国有色金属学报,2017,27(2):234-242.
[7]Chen Z,Zhao K,Fan L.Combinative hardening effects of precipitation in a commercial aged Al-Cu-Li-X alloy[J].Materials Science&Engineering A,2013,588(24):59-64.
[8]Hasan A F,Bennett C J,Shipway P H,et al.The influence of precipitation on plastic deformation of Al-Cu-Li alloys[J].Acta Materialia,2013,61(11):4010-4021.