本文通过在超细纤维合成革皮基中加入不同类型的阻燃剂,如十溴二苯乙烷、聚磷酸铵、氢氧化镁,进而对其阻燃性、柔软性、剥离性能、密度、SEM进行分析,结果显示,三种阻燃剂均能提高超细纤维合成革皮基的密度,但均使皮基的物性下降,柔软度下降;阻燃效果尤以十溴二苯乙烷阻燃性能最佳,其次是聚磷酸铵,最后是氢氧化镁。
DBDPE,APP and magnesium hydroxide were added in ultra fiber skin and then the flame retardance,softness,peeling,density,SEM were also analysed.The results showed that the three kinds of flame retardants can improve the density of microfiber leather,but the physical properties decreased,softness declined; the flame retardant effects was good especially in decabromodiphenyl ethane flame retardant performance,followed by ammonium polyphosphate,and finally the magnesium hydroxide.
引文
[1]许志,顾建慧,范幼华,顾海云.PA6/LDPE不定岛纤维PA6岛相分布的研究[J].皮革科学与工程.2008,(5):18-21.
[2]曲建波,章川波,冯见艳,高富堂.尼龙6/低密度聚乙烯不定岛型海岛纤维生产技术[J].合成纤维.2007,(6):44-47.
[3]O sawa Katsumi.Production of Synthetic Leather.Japan:JP2191778(A).1990.
[4]张静,吴清国,赵亚娟.合成革用聚氨酯浆料阻燃性能的研究[J].科技信息,2008,(26):337-338.
[5]罗晓民,杨菲菲,冯见艳,李鹏妮.不同填料对水性聚氨酯合成革贝斯性能的影响[J].中国皮革,2014,(1):35-38.
[6]孟烨,王丹,刘杰.高分子溴系阻燃剂发展现状及前景[J].盐业与化工,2012,(1):8-11.
[7]刘继延,刘学清.含磷聚合物阻燃剂的研究进展[J].中国塑料,2011,25(1):25-30.
[8]李正元.无机阻燃剂在阻燃聚合物中的应用[J].精细化工.1990,(3):36-42.