摘要
为研究玄武岩纤维掺量对轻质陶粒混凝土性能的影响,制备了4种不同纤维掺量的陶粒混凝土试件,测试了不同龄期试件的抗压强度、抗折强度和表观密度。结果表明:陶粒混凝土立方体试件抗压强度随着玄武岩纤维掺量的增大先增加后降低;陶粒混凝土表观密度随着纤维掺量的增大而逐渐降低,但不显著;陶粒混凝试件抗折强度随纤维掺量增大不断提高。
In order to study the effect of basalt fiber dosage on the properties of lightweight aggregate concrete, four kinds of ceramsite concrete with different fiber content of the specimen were prepared. The compressive strength, the flexural strength and the apparent density of specimens at different ages were tested. The results show that the compressive strength of ceramsite concrete cube specimen increases first and then decreases with the increase of the basalt fiber content, the apparent density decreases with the increase of fiber content of ceramsite concrete, but not significantly, and the flexural strength of ceramsite concrete increases with the increase of fiber content.
引文
[1]童伟光,黄锦恒,许松宜.纤维掺量对聚丙烯粗纤维陶粒混凝土力学性能的影响[J].广西科技大学学报,2014(2):17-20.
[2]夏多田,何明胜,唐艳娟,等.轻质混凝土砌块砌体受压性能试验研究[J].建筑科学,2013(7):44-48.
[3]夏多田,姜曙光,唐艳娟,等.灌孔复合陶粒混凝土砌块砌体力学性能试验研究[J].混凝土,2014(2):128-132.
[4]杨明宇,谢卫红.钢纤维页岩陶粒混凝土SHPB试验研究[J].混凝土与水泥制品,2015(12):54-57.
[5]谢尔盖,李中郢.玄武岩纤维材料的应用前景[J].纤维复合材料,2003(3):17-20.
[6]Jin Qiu Dong.Mechanical Properties of Basalt Fiber Rein forced Concrete at Low Cycle Impact[J].Applied Mechanics and Materials,2012,1801:174.
[7]Ayman M.M.Abdelhaleem,Mohammed Y.Abdellah,Hesham I.Fathi,et al.Mechanical Properties of ABS Embedded with Basalt Fiber Fillers[J].Journal for Manufacturing Science and Production,2016,16:2.
[8]董进秋,杜艳廷,闻宝联,等.玄武岩纤维混凝土力学性能与增韧机理研究[J].工业建筑,2011(S1):638-641.
[9]李为民,许金余.玄武岩纤维对混凝土的增强和增韧效应[J].硅酸盐学报,2008(4):476-481,486.
[10]吕开清,夏多田,杨士珏,等.新型陶粒混凝土材料配合比试验研究[J].混凝土,2017(4):147-150.