硅藻土的改性及其在含铜废水处理中的应用
|
摘要
以硅藻土为原料,利用焙烧、新生碳酸钙以及十二烷基磺酸钠进行改性活化,并用来处理含铜废水,探究硅藻土的最佳改性条件.研究结果表明,新生碳酸钙改性硅藻土对铜离子的去除效果最好,其最佳改性条件为:新生碳酸钙浓度为1.0 mol/L,改性温度为40℃,改性时间为80 min,去除率最高为99.9%.
The diatomite as a raw material was modified by roasting,newborn calcium carbonate and sodium dodecyl sulfonate,and then used for treating copper-containing wastewater so as to explore the optimum modification conditions.The results show that the newborn calcium carbonate modified diatomite has the best effect on the removal of copper ions.The optimum modification conditions were as follows:the newborn calcium carbonate concentration was 1.0 mol/L,the modification temperature was 40 °C,the modification time was 80 min,and the highest removal rate was 99.9%.
The diatomite as a raw material was modified by roasting,newborn calcium carbonate and sodium dodecyl sulfonate,and then used for treating copper-containing wastewater so as to explore the optimum modification conditions.The results show that the newborn calcium carbonate modified diatomite has the best effect on the removal of copper ions.The optimum modification conditions were as follows:the newborn calcium carbonate concentration was 1.0 mol/L,the modification temperature was 40 °C,the modification time was 80 min,and the highest removal rate was 99.9%.
引文
[1]高如琴,郑水林,刘月,等.硅藻土基多孔陶瓷的制备及其对孔雀石绿的吸附和降解[J].硅酸盐学报,2008,36(1):21-24.
[2]赵芳玉,薛洪海,李哲,等.低品位硅藻土吸附重金属的研究[J].生态环境学报,2010,19(12):2978-2981.
[3]谭凌智,祁士华,严存杰,等.改性硅藻土去除水中4种HCH的性能研究[J].中国环境科学,2011,31(6):916-920.
[4]朱健,王平,雷明婧,等.硅藻土的复合改性及其对水溶液中Cd2+的吸附特性[J].环境科学学报,2016,36(6):2059-2066.
[5]许树成.硅藻土开发应用与特性研究[J].阜阳师范学院学报,2000,20(3):30-32.
[6]李晓斌,魏成兵.硅藻土在废水处理中的应用[J].江苏环境科技,2008,21(2):71-74.
[7]李门楼.改性硅藻土处理含锌电镀废水的研究[J].湖南科技大学学报(自然科学版),2004,19(3):81-84.
[8]LI X W,LI X X,WAN G C.Surface modification of diatomite using polyaniline[J].Materials Chemistry and Physics,2007,102:140-143.
[9]李仁炳,丁社光.硅藻土吸附Cu2+吸附平衡等温式及穿透曲线的测定[J].重庆工商大学学报(自然科学版),2008,25(3):286-288.
[10]王代芝,倪琳.改性硅藻土处理含铜废水的实验研究[J].工业用水与废水,2012,43(6):33-35.
[11]陈鑫.改性硅藻土吸附废水中Ni2+的实验研究[D].昆明:昆明理工大学,2015.
[12]于瑞莲,胡恭任.焙烧改性膨润土处理垃圾渗滤液[J].华侨大学学报(自然科学版),2004,25(4):425-426.
[13]杨婷,王洪良,吕春欣,等.改性硅藻土对重金属离子的吸附规律[J].吉林大学学报(理学版),2012,50(4):815-820.
[14]廖经慧.硅藻土吸附剂的制备及其对重金属离子吸附性能的研究[D].北京:中国地质大学(北京),2012.
[15]袁迪,王莹.硅藻土吸附工业废水中汞离子的研究[J].环境保护科学,2005(7):27-31.
[16]赵丛.有机改性膨润土对重金属的吸咐机理研究[D].济南:山东师范大学,2011.
[17]夏士朋,石城.改性硅藻土处理废水中重金属离子[J].河南化工,2002(5):24-25.
[18]杨文,王平,朱健,等.PAM表面改性硅藻土吸附废水Pb2+[J].非金属矿,2011,34(2):54-58.
[2]赵芳玉,薛洪海,李哲,等.低品位硅藻土吸附重金属的研究[J].生态环境学报,2010,19(12):2978-2981.
[3]谭凌智,祁士华,严存杰,等.改性硅藻土去除水中4种HCH的性能研究[J].中国环境科学,2011,31(6):916-920.
[4]朱健,王平,雷明婧,等.硅藻土的复合改性及其对水溶液中Cd2+的吸附特性[J].环境科学学报,2016,36(6):2059-2066.
[5]许树成.硅藻土开发应用与特性研究[J].阜阳师范学院学报,2000,20(3):30-32.
[6]李晓斌,魏成兵.硅藻土在废水处理中的应用[J].江苏环境科技,2008,21(2):71-74.
[7]李门楼.改性硅藻土处理含锌电镀废水的研究[J].湖南科技大学学报(自然科学版),2004,19(3):81-84.
[8]LI X W,LI X X,WAN G C.Surface modification of diatomite using polyaniline[J].Materials Chemistry and Physics,2007,102:140-143.
[9]李仁炳,丁社光.硅藻土吸附Cu2+吸附平衡等温式及穿透曲线的测定[J].重庆工商大学学报(自然科学版),2008,25(3):286-288.
[10]王代芝,倪琳.改性硅藻土处理含铜废水的实验研究[J].工业用水与废水,2012,43(6):33-35.
[11]陈鑫.改性硅藻土吸附废水中Ni2+的实验研究[D].昆明:昆明理工大学,2015.
[12]于瑞莲,胡恭任.焙烧改性膨润土处理垃圾渗滤液[J].华侨大学学报(自然科学版),2004,25(4):425-426.
[13]杨婷,王洪良,吕春欣,等.改性硅藻土对重金属离子的吸附规律[J].吉林大学学报(理学版),2012,50(4):815-820.
[14]廖经慧.硅藻土吸附剂的制备及其对重金属离子吸附性能的研究[D].北京:中国地质大学(北京),2012.
[15]袁迪,王莹.硅藻土吸附工业废水中汞离子的研究[J].环境保护科学,2005(7):27-31.
[16]赵丛.有机改性膨润土对重金属的吸咐机理研究[D].济南:山东师范大学,2011.
[17]夏士朋,石城.改性硅藻土处理废水中重金属离子[J].河南化工,2002(5):24-25.
[18]杨文,王平,朱健,等.PAM表面改性硅藻土吸附废水Pb2+[J].非金属矿,2011,34(2):54-58.