摘要
以二羟甲基丙酸(DMPA)为亲水扩链剂,聚己二酸1,4-丁二醇酯多元醇(PBA)为软段,甲苯二异氰酸酯(TDI)为硬段,制备了亲水性聚氨酯预聚体;将亲水性聚氨酯预聚体用碱中和后,加入到氨基改性中空微球分散体中,高速剪切分散,亲水聚氨酯预聚体与改性中空微球发生接枝反应,获得水性聚氨酯接枝改性的中空微球(WPU-g-HM)乳液。将WPU-g-HM乳液涂敷在PVC基材上成膜,测试其消光性能。结果表明:WPU-g-HM乳液稳定性好,具有良好的成膜性能;胶膜表面光滑,外观柔和,富弹性触感,耐热性提高。WPU-g-HM乳液涂覆的PVC基材的光泽(60°)小于2°,属于平光范围,具有优异的自消光性能,还可用作遮盖性颜料和手感改性剂等应用于涂料、造纸、皮革等行业。
A hydrophilic polyurethane prepolymer was prepared with dimethyl propionic acid(DMPA) as a hydrophilic extender,poly(adipic acid 1,4-butanediol polyol)(PBA) as soft segment,and toluene diisocyanate(TDI) as hard segment,which was then neutralized by triethylamine(TEA) and added into the amino modified hollow polymethyl methacrylate(PMMA) microsphere dispersion under high speed shear to obtain a waterborne polyurethane(WPU) grafted PMMA hollow microsphere(WPU-g-HM) emulsion. The as-prepared WPU-g-HM emulsion was coated on PVC substrate to form a thin film. The results showed that a fairly stable WPU-g-HM emulsion was obtained with good film-forming properties,which exhibited smooth surface,soft appearance,elastic touch,and enhanced thermal stability. The glossiness(60°) of WPU-g-HM coated PVC was below 2° determined by the light glossiness meter,which came into the flat light range. The WPU-g-HM resin demonstrated excellent self-matting properties,which could be also used as hiding pigment and touch-feeling modifier for coatings,paper making and leather industries.
引文
[1]罗晓民,魏梦媛,冯见艳,等.高固含量水性聚氨酯的制备及其在超细纤维合成革上的应用[J].涂料工业,2018,48(2):64-68.
[2]王小荣,朱文婷,王新亮.双重改性聚氨酯丙烯酸酯的制备及应用性能[J].涂料工业,2017,47(3):31-36,43.
[3]王武生.水性聚氨酯涂料光泽控制---理论与实践[J].涂料工业,2018,48(6):75-82,87.
[4]庞浩,雍奇文,廖兵,等.一种反应自消光型水性聚氨酯树脂及其制备方法与应用:CN104974324A[P].2015-10-14.
[5]丁琳,杨建军,吴庆云,等.内交联水性聚氨酯自消光树脂的制备及表征[J].精细化工,2017,34(12):1334-1339.
[6]黄彦文.水性自消光树脂的合成与应用[J].涂层与防护,2018,39(3):34-38.
[7]张娜,王妮,施楣梧,等.球形中空微粒的可见光消光特性[J].纺织学报,2012,33(6):1-5.
[8]荆春贵,孙大庆.热膨胀性中空微球皮革消光补伤剂的研制[J].皮革化工,2003,19(6):20-22.
[9]ZHANG J A,YANG J J,WU Q Y,et al.SiO2/polymer hybrid hollow microspheres via double in situ miniemulsion polymerization[J].Macromolecules,2010,43(3),1188-1190.
[10]ZHANG J A,LIU Q,YANG B B,et al.Facile fabrication of double-shelled hollow microspheres via double in situ miniemulsion polymerization[J].Polymer Chemistry,2012,3,2720-2722.
[11]ZHANG J A,GE X W,WANG M Z,et al.Hybrid hollow microspheres templated from double Pickering emulsions[J].Chemical Communications,2010,46,4318-4320.
[12]王海波,李楚璇,杜宗良,等.氨基硅烷偶联剂对改性水性聚氨酯胶膜性能的影响[J].涂料工业,2016,46(8):47-52.