摘要
讨论了前处理、抛光液配方、温度、时间等因素对H65黄铜拉链抛光效果的影响,确定了仿金牙色的最佳抛光工艺为:过氧化氢600~750 mL/L,硫酸8~15 mL/L,增亮剂3~5 mL/L,乙醇60~90 mL/L,脂肪醇聚氧乙烯醚(AEO-9)0.4~0.8 g/L,温度20~30℃,时间2~3 min。该工艺抛光的黄铜拉链牙色光亮均匀,达到18K金的效果,而且抛光液稳定,使用寿命长,操作简单,维护方便,污染小。该工艺也适用于其他H65黄铜制品的仿金抛光。
The effects of pretreatment, polishing bath composition, temperature and time on polishing effectiveness of H65 brass zipper were discussed. The optimal polishing process conditions for gold-imitation teeth effect were obtained as follows: hydrogen peroxide 600-750 mL/L, sulfuric acid 8-15 mL/L, brightening agent 3-5 mL/L, ethanol 60-90 mL/L, fatty alcohol polyoxyethylene ether(AEO-9) 0.4-0.8g/L, temperature 20-30 ℃ and time 2-3 min. The brass zipper teeth color obtained thereunder is bright and uniform, achieving the effect of 18 K gold. The polishing bath features high stability, long service life, simple operation, easy maintenance and less pollution. The process is applicable to polishing of other H65 brass products.
引文
[1]谢光荣.黄铜拉链常温着色新工艺[J].材料保护,2004,37(11):40-41.
[2]赖俐超,唐春保,吴春伟,等.黄铜拉链深红古铜着色工艺[J].材料保护,2012,45(9):46-47.
[3]谢洪波,张来祥.黄铜拉链黑古铜工艺研究[J].电镀与涂饰,1992,11(1):57-59.
[4]刘新庆,邵忠财.铜拉链着黑古铜色[J].电镀与环保,2012,32(6):7-9.
[5]张丰如,赖俐超,唐春保,等.黄铜拉链黑古铜色着色新工艺[J].材料保护,2014,47(1):62-63.
[6]周栋,王瑀,丁毅,等.黄铜拉链化学镀锡工艺研究[J].表面技术,2010,39(2):58-60.
[7]赖俐超,张丰如,唐春保,等.黄铜拉链化学镀锡银牙苯并三氮唑钝化防变色工艺[J].材料保护,2014,47(3):34-36.
[8]方景礼.金属的化学抛光技术:第三部分──铜及铜合金制件的化学抛光[J].电镀与涂饰,2005,24(10):36-41.
[9]吕雪飞,李淑英.环保型铜及其合金化学抛光与钝化新工艺[J].材料保护,2006,39(9):25-27.
[10]石磊,王士磊,吴笛.环保型铜及铜合金化学抛光与钝化工艺[J].材料保护,2003,36(9):54-55.
[11]张婕,梁成浩,王鹏,等.铜及其合金的化学抛光工艺研究[J].表面技术,2006,35(6):43-45.
[12]农兰平,李金莲,巩育军.铜及铜合金不同化学抛光工艺研究[J].电镀与涂饰,2011,30(8):40-44.
[13]赖俐超,张丰如,唐春保.低碱环保型金属除油剂的研制[J].材料保护,2015,48(3):57-58,63.
[14]曾华梁,吴仲达,陈钧武,等.电镀工艺手册[M].2版.北京:机械工业出版社,2005:315.