沥青包覆人造石墨炭化处理工艺
|
摘要
为了提高人造石墨包覆后的炭化收率和电化学性能,本文采用改性沥青对人造石墨进行包覆,并经预氧化处理后再炭化。采用激光粒度分布仪、振实密度仪和比表面及孔径测试仪对炭化样品进行表征,并进一步对其电化学性能进行了研究。结果表明:炭化过程加入预氧化处理,有效地改善了结块现象,并极大的提高了负极材料的电化学性能。
In order to improve the carbonization yield and electrochemical properties of arti?cial graphite, the artificial graphite is coated with modified asphalt and carbonized after preoxidation treatment. The carbonized samples were characterized by laser particle size distributor,densitometer and specific surface and aperture tester, and the electrochemical performance was further studied. The results show that the preoxidation treatment in the carbonization process can effectively improve the agglomeration phenomenon and greatly improve the electrochemical properties of the cathode materials.
In order to improve the carbonization yield and electrochemical properties of arti?cial graphite, the artificial graphite is coated with modified asphalt and carbonized after preoxidation treatment. The carbonized samples were characterized by laser particle size distributor,densitometer and specific surface and aperture tester, and the electrochemical performance was further studied. The results show that the preoxidation treatment in the carbonization process can effectively improve the agglomeration phenomenon and greatly improve the electrochemical properties of the cathode materials.
引文
[1]张晓波,叶学海.包覆处理对提高人造石墨负极材料性能的研究[J].无机盐工业,2015,47(8):80-82.ZHANG Xiaobo,YE Xuehai.Research on improvement of properties of synthetic graphite anode battery material by doping treatment[J].Inorganic Chemicals Industry,2015,47(8):80-82.
[2]董永利,王东,宋微娜,等.碳包覆球形石墨负极材料的合成[J].黑龙江大学工程学报,2016,7(1):35-40.DONG Yongli,WANG Dong,SONG Weina,et al.Preparation of carbon coated spherical negative electrode materials[J].Journal of Engineering of Heilongjiang University,2016,7(1):35-40.
[3]鲍海友,田东,谌江宏,等.树脂包覆天然石墨用作锂离子电池负极材料的研究[J].电池工业,2013,18(1/2):7-17.BAO Haiyou,TIAN Dong,CHEN Jianghong,et al.Research of resin coating natural graphite for negative electrode m aterials of Li-ion battery[J].Chinese Battery Industry,2013,18(1/2):7-17.
[4]肖海河,刘洪波,何月德.沥青炭包覆微晶石墨用作锂离子电池负极材料的研究[J].功能材料,2013,44(19):2759-2763.XIAO Haihe,LIU Hongbo,HEYuede.Study on coal-tar pitch carbon coated microcry stalline graphite used as lithium ion batteries anode[J].Functional Materials,2013,44(19):2759-2763.
[2]董永利,王东,宋微娜,等.碳包覆球形石墨负极材料的合成[J].黑龙江大学工程学报,2016,7(1):35-40.DONG Yongli,WANG Dong,SONG Weina,et al.Preparation of carbon coated spherical negative electrode materials[J].Journal of Engineering of Heilongjiang University,2016,7(1):35-40.
[3]鲍海友,田东,谌江宏,等.树脂包覆天然石墨用作锂离子电池负极材料的研究[J].电池工业,2013,18(1/2):7-17.BAO Haiyou,TIAN Dong,CHEN Jianghong,et al.Research of resin coating natural graphite for negative electrode m aterials of Li-ion battery[J].Chinese Battery Industry,2013,18(1/2):7-17.
[4]肖海河,刘洪波,何月德.沥青炭包覆微晶石墨用作锂离子电池负极材料的研究[J].功能材料,2013,44(19):2759-2763.XIAO Haihe,LIU Hongbo,HEYuede.Study on coal-tar pitch carbon coated microcry stalline graphite used as lithium ion batteries anode[J].Functional Materials,2013,44(19):2759-2763.