铝合金环保型化学转化处理研究现状及展望
|
摘要
综述了国内外铝合金环保型的化学转化处理工艺的研究现状。介绍了无机盐转化膜(如钼酸盐转化膜、高锰酸盐转化膜、钛锆系盐转化膜等)、有机盐转化膜、稀土转化膜和稀土复合化学转化膜的研究进展,分析了各转化膜的性能特点,提出了现阶段存在的问题及解决途径,展望了铝合金未来无铬化学转化处理的研究方向。
The research status of environment-friendly chemical transformation treatment on aluminum alloys both at home and abroad is reviewed,including inorganic conversion coating such as molybdate conversion coating,permanganate conversion coating,Ti-Zr conversion coating,organic compound conversion coating,rare earth conversion coating and rare earth compound conversion coating. The performance characteristics of the conversion coatings above are analyzed,with the existing problems and solutions at the present stage put forward as well. The prospect for the research direction of chromium-free chemical transformation treatment on aluminum alloys in the future is shared.
The research status of environment-friendly chemical transformation treatment on aluminum alloys both at home and abroad is reviewed,including inorganic conversion coating such as molybdate conversion coating,permanganate conversion coating,Ti-Zr conversion coating,organic compound conversion coating,rare earth conversion coating and rare earth compound conversion coating. The performance characteristics of the conversion coatings above are analyzed,with the existing problems and solutions at the present stage put forward as well. The prospect for the research direction of chromium-free chemical transformation treatment on aluminum alloys in the future is shared.
引文
[1]李文刚,张晓丰,吕勤秀,等. LF21铝合金稀土转化膜的开裂及其钼酸盐后处理[J].腐蚀与防护,2009,30(4):248-275.
[2]ZHANG D Q,JIN X,XIE B,et al. Corrosion inhibition of ammonium molybdate for AA6061 alloy in Na Cl solution and its synergistic effect with calcium gluconate[J]. Surface and Interface Analysis,2012,44(1):78-83.
[3]徐临超,陈贤杭,李勇. 7075铝合金表面钼酸盐钝化工艺[J].浙江工贸职业技术学院学报,2015,15(2):50-52.
[4]许龙,郭瑞光,唐长斌,等.铝合金表面金黄色转化膜的研究[J].表面技术,2011,40(1):78-80.
[5]吴友恒,黎学明,杨文静,等. LY12铝合金的锰酸盐导电化学转化膜制备与表征[J].表面技术,2011,40(1):81-85.
[6]王爱荣,陶建中,马春全.铝合金表面黑色化学转化工艺及膜层耐腐蚀性能[J].材料保护,2009,42(11):36-37.
[7]葛圣松,杨玉香,邵谦.铸铝表面无铬黑色转化膜的形貌及耐蚀性[J].腐蚀化学与防护技术,2006,18(3):228-230.
[8]陈东初,潘炜盛.铝合金表面制备耐腐蚀性氧化膜的无铬处理液及其处理使用方法:中国,101054664[P]. 2007.
[9]郭瑞光,李晓杰,唐长斌,等.铸铝表面绿色环保化学处理新工艺[J].电镀与涂饰,2010,29(4):22-24.
[10]张力,郭瑞光,房新建,等.紫外辐射对2024铝合金表面钛盐转化膜形成的影响[J].表面技术,2012,41(1):1-4+16.
[11]曾丝丝.铝合金表面钛-钨复合化学转化膜制备工艺及性能研究[D].大连:大连交通大学,2010.
[12]李双保,陈礼扬,张小林,等. 5052铝合金Ti-Ce转化膜的性能[J].材料保护,2012,45(8):18-20.
[13]陈泽民,高梦颖,杨红贤.铝合金无铬化学转化膜工艺研究[J].电镀与涂饰,2015,34(7):391-395.
[14]王春霞,杨晓燕.铝合金表面锆盐转化膜的制备及其性能[J].材料保护,2010,43(2):36-37.
[15]肖鑫,许律,邓桎轩,等.铝及铝合金无铬氟锆酸盐化学转化膜[J].电镀与涂饰,2011,30(10):37-40.
[16]安成强,王双红,赵时璐,等.铝合金表面氧化锆转化膜的结构与性能[J].电镀与精饰,2012,34(6):1-4.
[17]陈廷益,路文,李文芳,等. AA6063铝合金Zr黑灰色转化膜及其自修复性能[J].中国腐蚀与防护学报,2015,35(2):177-182.
[18]王娇,郭瑞光. 2024铝合金表面钒锆复合转化膜的制备及其性能[J].材料保护,2014,47(3):1-4.
[19]姜琴.铝合金有机无机复合无铬钝化膜耐蚀性研究[D].北京:中国科学院研究生院,2013.
[20]张贺宏,张晓丰,赵旭辉,等. 5052铝合金表面钛锆基转化膜的制备及耐蚀性[J].表面技术,2015(5):38-42.
[21]尚守研.铝合金预处理及无铬化学转化膜制备工艺研究[D].秦皇岛:燕山大学,2015.
[22]王双红.铝合金表面钛-锆-有机膦酸盐复合膜的制备与性能[D].沈阳:东北大学,2009.
[23]杜文朝.铝合金钛锆盐转化膜的制备与性能研究[D].秦皇岛:燕山大学,2012.
[24]刘晓辉.铝合金无铬有色化学转化工艺的研究[D].北京:机械科学研究总院,2014.
[25]易爱华.铝合金表面钛/锆转化膜的着色及性能优化[D].广州:华南理工大学,2012.
[26]易爱华,黎雪芬,李文芳,等.铝合金表面有色转化膜快速成膜工艺[J].电镀与涂饰,2014,33(12):519-523.
[27]陈延益. 6063铝合金表面着色锆-钛-无铬转化膜的成膜及其机理研究[D].广州:华南理工大学,2011.
[28]刘浩威. 6063铝合金钛锆系钝化液稳定性研究[D].广州:华南理工大学,2014.
[29]廖忠淼,李文芳,穆松林,等.铝合金钛锆转化膜槽液消耗规律的研究[J].表面技术,2017,46(1):51-55.
[30]刘超.铝合金三价铬复合转化膜制备及性能研究[D].广州:广东工业大学,2016.
[31]李国栋.环保型铝合金三价铬转化膜制备及腐蚀性能研究[D].银川:宁夏大学,2014.
[32]彭敬东,邓传跃,石燕,等.一种用于处理铝合金的三价铬本色钝化液:中国,201010533461. 7[P]. 2010.
[33]杨显芳,梁天权,韦唯,等.环保型铝合金表面转化处理的研究进展[J].材料导报,2014(2):439-442.
[34]陈思屹. ADC12铝合金上稀土钝化膜制备工艺与防腐蚀性能的研究[D].重庆:重庆大学,2016.
[35]付贵.铝合金表面稀土转化膜技术研究[D].成都:西南石油大学,2016.
[36]陈东初,李文芳,龚伟慧,等.铝合金表面无铬化学转化膜的制备及其性能[J].中国有色金属学报,2008,18(10):1841-1844.
[37]王春霞,周雅,曹经倩,等.铝合金稀土盐钝化工艺研究[J].电镀与精饰,2010,32(10):32-33.
[38]张军军.铝合金表面Ce-Mn转化膜常温制备及表征[D].广州:华南理工大学,2010.
[39]宫承鹏,王昕,王浩泉,等.不同添加剂对铝表面铈转化膜耐蚀性的影响[J].中国稀土学报,2011,29(2):212-216.
[40]陈礼扬.铝合金表面无铬转化膜的制备工艺及性能研究[D].南昌:南昌大学,2012.
[41]凡婷. 6063铝合金表面Ce-Mn/Mo复合转化膜制备工艺及性能研究[D].广州:华南理工大学,2012.
[42]YANG X F,LIANG T Q,WEI W,et al. Study on preparation and the characteristics of environment-friendly Ce-Ti-Mn conversion coating on aluminum alloy 6061[J]. Advanced Materials Research,2014,881-883:1385-1390.
[2]ZHANG D Q,JIN X,XIE B,et al. Corrosion inhibition of ammonium molybdate for AA6061 alloy in Na Cl solution and its synergistic effect with calcium gluconate[J]. Surface and Interface Analysis,2012,44(1):78-83.
[3]徐临超,陈贤杭,李勇. 7075铝合金表面钼酸盐钝化工艺[J].浙江工贸职业技术学院学报,2015,15(2):50-52.
[4]许龙,郭瑞光,唐长斌,等.铝合金表面金黄色转化膜的研究[J].表面技术,2011,40(1):78-80.
[5]吴友恒,黎学明,杨文静,等. LY12铝合金的锰酸盐导电化学转化膜制备与表征[J].表面技术,2011,40(1):81-85.
[6]王爱荣,陶建中,马春全.铝合金表面黑色化学转化工艺及膜层耐腐蚀性能[J].材料保护,2009,42(11):36-37.
[7]葛圣松,杨玉香,邵谦.铸铝表面无铬黑色转化膜的形貌及耐蚀性[J].腐蚀化学与防护技术,2006,18(3):228-230.
[8]陈东初,潘炜盛.铝合金表面制备耐腐蚀性氧化膜的无铬处理液及其处理使用方法:中国,101054664[P]. 2007.
[9]郭瑞光,李晓杰,唐长斌,等.铸铝表面绿色环保化学处理新工艺[J].电镀与涂饰,2010,29(4):22-24.
[10]张力,郭瑞光,房新建,等.紫外辐射对2024铝合金表面钛盐转化膜形成的影响[J].表面技术,2012,41(1):1-4+16.
[11]曾丝丝.铝合金表面钛-钨复合化学转化膜制备工艺及性能研究[D].大连:大连交通大学,2010.
[12]李双保,陈礼扬,张小林,等. 5052铝合金Ti-Ce转化膜的性能[J].材料保护,2012,45(8):18-20.
[13]陈泽民,高梦颖,杨红贤.铝合金无铬化学转化膜工艺研究[J].电镀与涂饰,2015,34(7):391-395.
[14]王春霞,杨晓燕.铝合金表面锆盐转化膜的制备及其性能[J].材料保护,2010,43(2):36-37.
[15]肖鑫,许律,邓桎轩,等.铝及铝合金无铬氟锆酸盐化学转化膜[J].电镀与涂饰,2011,30(10):37-40.
[16]安成强,王双红,赵时璐,等.铝合金表面氧化锆转化膜的结构与性能[J].电镀与精饰,2012,34(6):1-4.
[17]陈廷益,路文,李文芳,等. AA6063铝合金Zr黑灰色转化膜及其自修复性能[J].中国腐蚀与防护学报,2015,35(2):177-182.
[18]王娇,郭瑞光. 2024铝合金表面钒锆复合转化膜的制备及其性能[J].材料保护,2014,47(3):1-4.
[19]姜琴.铝合金有机无机复合无铬钝化膜耐蚀性研究[D].北京:中国科学院研究生院,2013.
[20]张贺宏,张晓丰,赵旭辉,等. 5052铝合金表面钛锆基转化膜的制备及耐蚀性[J].表面技术,2015(5):38-42.
[21]尚守研.铝合金预处理及无铬化学转化膜制备工艺研究[D].秦皇岛:燕山大学,2015.
[22]王双红.铝合金表面钛-锆-有机膦酸盐复合膜的制备与性能[D].沈阳:东北大学,2009.
[23]杜文朝.铝合金钛锆盐转化膜的制备与性能研究[D].秦皇岛:燕山大学,2012.
[24]刘晓辉.铝合金无铬有色化学转化工艺的研究[D].北京:机械科学研究总院,2014.
[25]易爱华.铝合金表面钛/锆转化膜的着色及性能优化[D].广州:华南理工大学,2012.
[26]易爱华,黎雪芬,李文芳,等.铝合金表面有色转化膜快速成膜工艺[J].电镀与涂饰,2014,33(12):519-523.
[27]陈延益. 6063铝合金表面着色锆-钛-无铬转化膜的成膜及其机理研究[D].广州:华南理工大学,2011.
[28]刘浩威. 6063铝合金钛锆系钝化液稳定性研究[D].广州:华南理工大学,2014.
[29]廖忠淼,李文芳,穆松林,等.铝合金钛锆转化膜槽液消耗规律的研究[J].表面技术,2017,46(1):51-55.
[30]刘超.铝合金三价铬复合转化膜制备及性能研究[D].广州:广东工业大学,2016.
[31]李国栋.环保型铝合金三价铬转化膜制备及腐蚀性能研究[D].银川:宁夏大学,2014.
[32]彭敬东,邓传跃,石燕,等.一种用于处理铝合金的三价铬本色钝化液:中国,201010533461. 7[P]. 2010.
[33]杨显芳,梁天权,韦唯,等.环保型铝合金表面转化处理的研究进展[J].材料导报,2014(2):439-442.
[34]陈思屹. ADC12铝合金上稀土钝化膜制备工艺与防腐蚀性能的研究[D].重庆:重庆大学,2016.
[35]付贵.铝合金表面稀土转化膜技术研究[D].成都:西南石油大学,2016.
[36]陈东初,李文芳,龚伟慧,等.铝合金表面无铬化学转化膜的制备及其性能[J].中国有色金属学报,2008,18(10):1841-1844.
[37]王春霞,周雅,曹经倩,等.铝合金稀土盐钝化工艺研究[J].电镀与精饰,2010,32(10):32-33.
[38]张军军.铝合金表面Ce-Mn转化膜常温制备及表征[D].广州:华南理工大学,2010.
[39]宫承鹏,王昕,王浩泉,等.不同添加剂对铝表面铈转化膜耐蚀性的影响[J].中国稀土学报,2011,29(2):212-216.
[40]陈礼扬.铝合金表面无铬转化膜的制备工艺及性能研究[D].南昌:南昌大学,2012.
[41]凡婷. 6063铝合金表面Ce-Mn/Mo复合转化膜制备工艺及性能研究[D].广州:华南理工大学,2012.
[42]YANG X F,LIANG T Q,WEI W,et al. Study on preparation and the characteristics of environment-friendly Ce-Ti-Mn conversion coating on aluminum alloy 6061[J]. Advanced Materials Research,2014,881-883:1385-1390.