摘要
从钨酸盐的单掺杂离子,双掺杂离子等方面综述了掺杂稀土离子钨酸盐材料的发光特性研究情况,针对不同类型钨酸盐材料的不同制备方法做了系统的介绍。根据目前研究得出,稀土离子掺杂可以获得性能优良的钨酸盐发光材料,水热法、化学沉淀法、高温固相法、微弧氧化法等方法是制备钨酸盐发光的重要手段。
From the single ion doped tungstate AND double doped ions began,the luminescent properties of rare earth ions doped tungstate,and different preparation methods for different types of tungstate were simple introduced.
引文
[1]Dabrea K V,Dhobleb S J,Lochabc J.[J].2012,149(3):348-352.
[2]Aleksandrova L,Iordanovaa R,Dimitrievbetal Y.[J].Optical Materials,2014,36(8):1366-1372.
[3]Sun J S,Yu T T,Li X P,et al.[J].Journal of Physics and Chemistry of Solids,2012,73(3):465-470.
[4]Huang Y L,Seo H J,Yang Y,et al.[J].Materials Chemistry&Physics,2005,91(2):424-430.
[5]宋术岩,韩维强,张洪杰.[J].高等学校化学学报,2011,32(3):508-514.
[6]Piskua Z,Czajka J,Staninski K,et al.[J].Journal of Rare Earths,2014,32(3):221-225.
[7]Mateos X,Soléa R,Gavaldàetal J.[J].Optical Materials,2006,28(5):519-523.
[8]冯晓辉,孟庆裕,孙江亭,等.[J].物理学报,2011,60(3):037806-1-037806-9.
[9]骆永石,张家骅,张霞.[J].中国光学与应用光学,2009,2(1):54-59.
[10]Babua A M,Jamalaiahb B C,Chengaiahaetal T.[J].Physica B:Condensed Matter,2011,406(15/16),3074-3078.
[11]Grobelna B,Lipowska B,Konkowski A M.[J].Journal of Alloys and Compounds,2006,419(1/2):191-196.
[12]沈祥,聂秋华,徐铁峰,等.[J].物理学报,2005,54(5):2379-2382.
[13]李晶晶,孙佳石,张金苏,等.[J].发光学报,2013,34(4):400-405.
[14]李梦娜,雷芳,陈昊鸿,等.[J].无机材料学报,2013,28(12):1281-1285.
[15]刘磊,杨魁胜,贺超,等.[J].无机材料学报,2013,29(6):1123-1128.
[16]Bouzidia C,Ferhia M,Elhouicheta H,et al.[J].Journal of Luminescence,2015,161(3):448-455.
[17]Wei Z,Zheng W,Zhu Z Y,et al.[J].Chemical Physics Letters,2016,65(3):46-49.
[18]任艳东,吕树臣.[J].物理学报,2011,60(8):087804-1-087804-6.
[19]Alfaro S O,Cruz A M.[J].Applied Catalysis A:General,2010,383(1/2):128-133.
[20]徐冰玉,王国凤,李莹,等.[J].发光学报,2013,34(9):1178-1182.
[21]Li Y H,Huang J F,Yin J,et al.[J].Materials Letters,2014,135(11):168-171.
[22]梁锋,胡义华,陈丽,等.[J].物理学报,2013,62(18):183302-1-183302-8.
[23]Tomaszewicz E,Fuks H,Typek J.[J].Thermochimica Acta,2013,568(20):95-103.
[24]何剑,蔡启舟,肖枫,等.[J].催化学报,2009,30(11):1137-1142.
[25]洪慧敏,吕忆农,刘云飞,等.[J].硅酸盐学报,2012,40(7):1023-1029.
[26]Hanh PV,Hoang L H,Hai P V.[J].Journal of Physics and Chemistry of Solids,2013,74(11):426-430.