PA6导热复合材料研究现状
|
摘要
相比于金属材料,导热高分子材料具有密度、热膨胀系数低,耐腐蚀性能好,加工工艺适应性强等优点,因此成为材料学者研究的热点之一。本文就目前聚酰胺6(PA6)导热复合材料常用的研究方法及导热填料进行了综述。
Thermal conductive polymer has more advantages than metal, such as low density, low thermal expansion coefficient, good corrosion resistance, easy forming and so on. It is one of the research hotspots of material scholars. The recent advance of the research methods and the commonly used thermal conductive fi llers of polyamide 6(PA6) thermal conductive composites are reviewed in this paper.
Thermal conductive polymer has more advantages than metal, such as low density, low thermal expansion coefficient, good corrosion resistance, easy forming and so on. It is one of the research hotspots of material scholars. The recent advance of the research methods and the commonly used thermal conductive fi llers of polyamide 6(PA6) thermal conductive composites are reviewed in this paper.
引文
[1]肖琰,魏伯荣,杨海涛,等.高热高分子材料的研究开发现状[J].中国塑料,2005,19(4):12-16.
[2]麦伟宗,王飞,黄李胜,等.导热PA6复合材料导热性能的研究[J].合成材料老化与应用,2013(5):14-15,34.
[3]丁鹏,李军,张锦,等.Al2O3粒径与形貌对尼龙复合材料导热性能影响的研究[J].功能材料,2015,46(11):11 065-11 068.
[4]唐明明,容敏智,马传国,等.Al2O3的表面处理及粒子尺寸对SBR导热橡胶性能的影响[J].合成橡胶工业,2003,26(2):104-107.
[5]刘举,王冲,付登强,等.导热绝缘PA6复合材料的制备及性能研究[J].绝缘材料,2018(4):18-20,27.
[6]林俊辉,姜宏伟.氧化锌填充PA6制备绝缘导热塑料的研究[J].绝缘材料,2013,46(4):30-34.
[7]李明辉,高智芳,罗红林,等.填充型尼龙6导热绝缘复合材料的性能及制备[J].塑料,2013,42(1):1-3.
[8]潘世濠,代培刚,陈英杰,等.AlN/PA6复合材料导热性能的研究[J].广州化工,2015,43(11):83-84,108.
[9]步真松.SiC填充PA6导热复合材料的制备和研究[D].郑州:郑州大学,2013.
[10]刘经港.高性能导热PA6复合材料的制备及其性能研究[D].深圳:深圳大学,2016.
[11]吴惠民.石墨烯协同Al2O3导热PA6的制备及性能研究[J].橡塑技术与装备,2017,43(24):39-42.
[12]朱帅甫.面向LED散热器的导热复合材料的制备[D].郑州:河南工业大学,2016.
[13]郝喜东.高导热PA6/石墨复合材料的制备及性能[D].合肥:合肥工业大学,2015.
[14]周海堤,张强,陈光伟,等.不同粒径比复配填充对PA6/鳞片石墨复合材料导热性能的影响[J].塑料工业,2015,43(11):115-118,123.
[15]张宁,郭强,石文鹏,等.连续铝纤维制备PA6导热复合材料[J].高分子材料科学与工程,2016,32(4):159-162,167.
[2]麦伟宗,王飞,黄李胜,等.导热PA6复合材料导热性能的研究[J].合成材料老化与应用,2013(5):14-15,34.
[3]丁鹏,李军,张锦,等.Al2O3粒径与形貌对尼龙复合材料导热性能影响的研究[J].功能材料,2015,46(11):11 065-11 068.
[4]唐明明,容敏智,马传国,等.Al2O3的表面处理及粒子尺寸对SBR导热橡胶性能的影响[J].合成橡胶工业,2003,26(2):104-107.
[5]刘举,王冲,付登强,等.导热绝缘PA6复合材料的制备及性能研究[J].绝缘材料,2018(4):18-20,27.
[6]林俊辉,姜宏伟.氧化锌填充PA6制备绝缘导热塑料的研究[J].绝缘材料,2013,46(4):30-34.
[7]李明辉,高智芳,罗红林,等.填充型尼龙6导热绝缘复合材料的性能及制备[J].塑料,2013,42(1):1-3.
[8]潘世濠,代培刚,陈英杰,等.AlN/PA6复合材料导热性能的研究[J].广州化工,2015,43(11):83-84,108.
[9]步真松.SiC填充PA6导热复合材料的制备和研究[D].郑州:郑州大学,2013.
[10]刘经港.高性能导热PA6复合材料的制备及其性能研究[D].深圳:深圳大学,2016.
[11]吴惠民.石墨烯协同Al2O3导热PA6的制备及性能研究[J].橡塑技术与装备,2017,43(24):39-42.
[12]朱帅甫.面向LED散热器的导热复合材料的制备[D].郑州:河南工业大学,2016.
[13]郝喜东.高导热PA6/石墨复合材料的制备及性能[D].合肥:合肥工业大学,2015.
[14]周海堤,张强,陈光伟,等.不同粒径比复配填充对PA6/鳞片石墨复合材料导热性能的影响[J].塑料工业,2015,43(11):115-118,123.
[15]张宁,郭强,石文鹏,等.连续铝纤维制备PA6导热复合材料[J].高分子材料科学与工程,2016,32(4):159-162,167.