大型原油储罐导静电涂料的研究进展
|
摘要
综述了基于聚乙炔、聚苯胺等本征型和添加型(包括聚吡咯、碳系、金属、金属氧化物等)导静电涂料的研究进展,并指出原油储罐导静电涂料的研究热点和未来发展方向。
The research progress of intrinsic-type, which is mainly based on polyacetylene and polyaniline, and additive-type, using polypyrrole, carbon-based materials, metals and metal oxides as a filler, electrostatic conductive coatings was summarized. The research highlights and future development directions of electrostatic conductive coating used for crude oil storage tank were pointed out.
The research progress of intrinsic-type, which is mainly based on polyacetylene and polyaniline, and additive-type, using polypyrrole, carbon-based materials, metals and metal oxides as a filler, electrostatic conductive coatings was summarized. The research highlights and future development directions of electrostatic conductive coating used for crude oil storage tank were pointed out.
引文
[1]KASAI N,MAEDA T,TAMURA K,et al.Application of risk curve for statistical analysis of backside corrosion in the bottom floors of oil storage tanks[J].International Journal of Pressure Vessels and Piping,2016,141:19-25.
[2]TOKUTAKE K,NISHI H,ITO D,et al.Constant-phase element characteristics caused by resistivity distribution in high performance anti-corrosion organic coating applied to oil storage tank[J].ECS Transactions,2015,69(26):1-8.
[3]ZHOU P,LIANG J M,ZHANG F,et al.Influence of chromium on corrosion behavior of low-alloy steel in cargo oil tank O2–CO2–SO2–H2S wet gas environment[J].Journal of Iron and Steel Research International,2015,22(7):630-637.
[4]EL-GHAFFAR M A A,ABDEL-WAHAB N A,SANAD M A,et al.High performance anti-corrosive powder coatings based on phosphate pigments containing poly(o-aminophenol)[J].Progress in Organic Coatings,2015,78:42-48.
[5]LIU W M,ZHOU Q J,LI L S,et al.Effect of alloy element on corrosion behavior of the huge crude oil storage tank steel in seawater[J].Journal of Alloys and Compounds,2014,598:198-204.
[6]SHEN W N,FENG L J,LIU X,et al.Multiwall carbon nanotubes-reinforced epoxy hybrid coatings with high electrical conductivity and corrosion resistance prepared via electrostatic spraying[J].Progress in Organic Coatings,2016,90:139-146.
[7]JIANG J J,LIU J P,LIN H Q,et al.Growth of thin carbon nanotubes by catalytic decomposition of methane over Co–Mo/Mg O catalyst and their transparent conducting electrostatic properties[J].Fullerenes,Nanotubes and Carbon Nanostructures,2015,23(12):1086-1090.
[8]SAINI P,CHOUDHARY V,DHAWAN S K.Improved microwave absorption and electrostatic charge dissipation efficiencies of conducting polymer grafted fabrics prepared via in situ polymerization[J].Polymers for Advanced Technologies,2012,23(3):343-349.
[9]苏雅丽,彭毛来,杨名亮,等.油罐导静电涂料研究进展[J].上海涂料,2013,51(11):31-34.
[10]NIGREY P J,MACDIARMID A G,HEEGER A J.Electrochemistry of polyacetylene,(CH)x:electrochemical doping of(CH)x films to the metallic state[J].Journal of the Chemical Society,Chemical Communications,1979,96(14):594-595.
[11]宋林花,王国锋,姜翠玉,等.聚乙炔/活性碳复合材料的制备及其导电性能的研究[J].材料导报,2013,27(1):83-85,108.
[12]张学卿,王志超.聚氨酯油罐导电涂料[J].现代涂料与涂装,2007,10(9):36-39.
[13]MENGOLI G,MUNARI M T,BIANCO P,et al.Anodic synthesis of polyaniline coatings onto Fe sheets[J].Journal of Applied Polymer Science,1981,26(12):4247-4257.
[14]FANG J J,XU K,ZHU L H,et al.A study on mechanism of corrosion protection of polyaniline coating and its failure[J].Corrosion Science,2007,49(11):4232-4242.
[15]OLAD A,BARATI M,BEHBOUDI S.Preparation of PANI/epoxy/Zn nanocomposite using Zn nanoparticles and epoxy resin as additives and investigation of its corrosion protection behavior on iron[J].Progress in Organic Coatings,2012,74(1):221-227.
[16]谷亚新,刘运学,范兆荣,等.聚苯胺/环氧树脂导静电涂料的研制[J].新型建筑材料,2007,34(5):20-22.
[17]BAGHERZADEH M,HADDADI H,IRANPOUR M.Electrochemical evaluation and surface study of magnetite/PANI nanocomposite for carbon steel protection in 3.5%Na Cl[J].Progress in Organic Coatings,2016,101:149-160.
[18]蔡本慧,曹雷,王肇君.导电聚合物聚吡咯的制备、性质及其应用[J].化工科技市场,2010,33(5):11-16.
[19]张国标,姚伯龙,齐家鹏,等.纳米纤状聚吡咯导电涂料的制备与性能研究[J].涂料工业,2014,44(11):1-6.
[20]尚秀丽,孙林,胡中爱.导电聚吡咯/醋酸纤维素复合膜的合成及性能研究[J].化工新型材料,2008,36(1):62-63.
[21]路亮,侯文鹏,关士友,等.聚吡咯的绿色制备及其环氧树脂复合涂层对Q235钢的防腐性能[J].化工进展,2013,32(3):617-623.
[22]王发龙,郑燕升,莫春燕,等.聚吡咯/纳米Ce O2复合材料的制备及防腐性能研究[J].塑料工业,2014,42(12):119-122.
[23]杨超,王云普,郭金山,等.环境友好型氟碳导电涂料的研究[J].涂料工业,2007,37(增刊1):1-5.
[24]杨超,王云普,刑兰莹,等.炭系填料/水性叔氟导电涂料的性能研究[J].现代涂料与涂装,2008,11(7):24-26.
[25]莫斌,刘祥萱,吴友朋,等.炭黑/碳化硅复合导电涂料的制备及导电性能研究[J].现代涂料与涂装,2009,12(8):10-12.
[26]刘亚群,许佩新,章连众,等.炭系填充型导电复合材料电性能的研究[J].浙江大学学报(工学版),2004,38(2):253-256.
[27]王望,郭彦峰,孙振锋.碳系导电油墨填料的研究进展[J].化工进展,2015,34(12):4259-4264.
[28]中国科学院宁波材料技术与工程研究所,芜湖春风新材料有限公司.一种石墨烯/丙烯酸导静电涂料及其制备方法:201610353311.5[P].2016–10–12.
[29]LIU S,GU L,ZHAO H C,et al.Corrosion resistance of graphene-reinforced waterborne epoxy coatings[J].Journal of Materials Science&Technology,2016,32(5):425-431.
[30]GU L,LIU S,ZHAO H C,et al.Facile preparation of water-dispersible graphene sheets stabilized by carboxylated oligoanilines and their anticorrosion coatings[J].ACS Applied Materials&Interfaces,2015,7(32):17641-17648.
[31]刘栓,姜欣,赵海超,等.石墨烯环氧涂层的耐磨耐蚀性能研究[J].摩擦学学报,2015,35(5):598-605.
[32]刘栓,赵霞,赵文杰.海水环境下石墨烯基重防腐涂层耐磨耐蚀机理研究[C]//中国腐蚀与防护协会.全国第八届腐蚀大会学术会议论文集.[出版地不详:出版者不详],2015:36-37.
[33]王玉琼,刘栓,刘兆平,等.石墨烯掺杂水性环氧树脂的隔水和防护性能[J].电镀与涂饰,2015,34(6):314-319.
[34]姜振华,赵东辉,林立民,等.铜粉填充的导电涂料[J].涂料工业,1992,22(3):12-13.
[35]施冬梅,鲁彦玲,杜仕国.偶联剂对铜-环氧电磁屏蔽导电涂料的影响[J].中国涂料,2005,20(6):16-18.
[36]申蓓蓓,郭忠诚.塑料件用水性导电涂料的研制[J].涂料工业,2007,37(7):26-28,31.
[37]张心华,闫爱军.富镍导电涂层耐腐蚀性能研究[J].涂料工业,2015,45(3):1-6.
[38]张松,李永,刘增堂.水性镍系电磁屏蔽涂料的制备及导电性能研究[J].电子元件与材料,2006,25(10):65-67.
[39]史政海,张群安.浅色复合导电涂料[J].中国涂料,2004,19(7):30-32.
[40]杜仕国,刘小强,闫军,等.纳米ATO复合导电涂料的研制[J].北京理工大学学报,2007,25(增刊1):285-287.
[41]杨华明,胡岳华,张慧慧.重晶石基锑掺杂Sn O2导电粉末用于导电涂料及其屏蔽特性[J].功能材料,2006,37(9):1433-1435.
[42]余凤斌,陈莹.镀银铜粉导电涂料的制备及性能[J].电镀与涂饰,2012,31(9):63-65.
[43]吕维华,伍家卫,唐蓉萍,等.高氯化聚乙烯银包铜防腐导电涂料的研究[J].中国建材科技,2012,21(1):63-67.
[44]李哲男,黄昊,张雪峰,等.导电涂料中纳米铜粉抗氧化性的研究[J].材料科学与工艺,2008,16(6):826-829,834.
[45]张露露,游敏,吴建好,等.玻璃鳞片导电涂料的研究[J].电镀与涂饰,2007,26(2):32-34.
[46]谭宁,郭忠诚.电解行业用环氧导电防腐涂料的制备[J].电镀与涂饰,2008,27(12):49-51,54.
[47]姜才兴,周福根,张晓凌.浅色油罐氟碳导静电防腐涂料的研制[J].中国涂料,2008,23(1):15-19.
[2]TOKUTAKE K,NISHI H,ITO D,et al.Constant-phase element characteristics caused by resistivity distribution in high performance anti-corrosion organic coating applied to oil storage tank[J].ECS Transactions,2015,69(26):1-8.
[3]ZHOU P,LIANG J M,ZHANG F,et al.Influence of chromium on corrosion behavior of low-alloy steel in cargo oil tank O2–CO2–SO2–H2S wet gas environment[J].Journal of Iron and Steel Research International,2015,22(7):630-637.
[4]EL-GHAFFAR M A A,ABDEL-WAHAB N A,SANAD M A,et al.High performance anti-corrosive powder coatings based on phosphate pigments containing poly(o-aminophenol)[J].Progress in Organic Coatings,2015,78:42-48.
[5]LIU W M,ZHOU Q J,LI L S,et al.Effect of alloy element on corrosion behavior of the huge crude oil storage tank steel in seawater[J].Journal of Alloys and Compounds,2014,598:198-204.
[6]SHEN W N,FENG L J,LIU X,et al.Multiwall carbon nanotubes-reinforced epoxy hybrid coatings with high electrical conductivity and corrosion resistance prepared via electrostatic spraying[J].Progress in Organic Coatings,2016,90:139-146.
[7]JIANG J J,LIU J P,LIN H Q,et al.Growth of thin carbon nanotubes by catalytic decomposition of methane over Co–Mo/Mg O catalyst and their transparent conducting electrostatic properties[J].Fullerenes,Nanotubes and Carbon Nanostructures,2015,23(12):1086-1090.
[8]SAINI P,CHOUDHARY V,DHAWAN S K.Improved microwave absorption and electrostatic charge dissipation efficiencies of conducting polymer grafted fabrics prepared via in situ polymerization[J].Polymers for Advanced Technologies,2012,23(3):343-349.
[9]苏雅丽,彭毛来,杨名亮,等.油罐导静电涂料研究进展[J].上海涂料,2013,51(11):31-34.
[10]NIGREY P J,MACDIARMID A G,HEEGER A J.Electrochemistry of polyacetylene,(CH)x:electrochemical doping of(CH)x films to the metallic state[J].Journal of the Chemical Society,Chemical Communications,1979,96(14):594-595.
[11]宋林花,王国锋,姜翠玉,等.聚乙炔/活性碳复合材料的制备及其导电性能的研究[J].材料导报,2013,27(1):83-85,108.
[12]张学卿,王志超.聚氨酯油罐导电涂料[J].现代涂料与涂装,2007,10(9):36-39.
[13]MENGOLI G,MUNARI M T,BIANCO P,et al.Anodic synthesis of polyaniline coatings onto Fe sheets[J].Journal of Applied Polymer Science,1981,26(12):4247-4257.
[14]FANG J J,XU K,ZHU L H,et al.A study on mechanism of corrosion protection of polyaniline coating and its failure[J].Corrosion Science,2007,49(11):4232-4242.
[15]OLAD A,BARATI M,BEHBOUDI S.Preparation of PANI/epoxy/Zn nanocomposite using Zn nanoparticles and epoxy resin as additives and investigation of its corrosion protection behavior on iron[J].Progress in Organic Coatings,2012,74(1):221-227.
[16]谷亚新,刘运学,范兆荣,等.聚苯胺/环氧树脂导静电涂料的研制[J].新型建筑材料,2007,34(5):20-22.
[17]BAGHERZADEH M,HADDADI H,IRANPOUR M.Electrochemical evaluation and surface study of magnetite/PANI nanocomposite for carbon steel protection in 3.5%Na Cl[J].Progress in Organic Coatings,2016,101:149-160.
[18]蔡本慧,曹雷,王肇君.导电聚合物聚吡咯的制备、性质及其应用[J].化工科技市场,2010,33(5):11-16.
[19]张国标,姚伯龙,齐家鹏,等.纳米纤状聚吡咯导电涂料的制备与性能研究[J].涂料工业,2014,44(11):1-6.
[20]尚秀丽,孙林,胡中爱.导电聚吡咯/醋酸纤维素复合膜的合成及性能研究[J].化工新型材料,2008,36(1):62-63.
[21]路亮,侯文鹏,关士友,等.聚吡咯的绿色制备及其环氧树脂复合涂层对Q235钢的防腐性能[J].化工进展,2013,32(3):617-623.
[22]王发龙,郑燕升,莫春燕,等.聚吡咯/纳米Ce O2复合材料的制备及防腐性能研究[J].塑料工业,2014,42(12):119-122.
[23]杨超,王云普,郭金山,等.环境友好型氟碳导电涂料的研究[J].涂料工业,2007,37(增刊1):1-5.
[24]杨超,王云普,刑兰莹,等.炭系填料/水性叔氟导电涂料的性能研究[J].现代涂料与涂装,2008,11(7):24-26.
[25]莫斌,刘祥萱,吴友朋,等.炭黑/碳化硅复合导电涂料的制备及导电性能研究[J].现代涂料与涂装,2009,12(8):10-12.
[26]刘亚群,许佩新,章连众,等.炭系填充型导电复合材料电性能的研究[J].浙江大学学报(工学版),2004,38(2):253-256.
[27]王望,郭彦峰,孙振锋.碳系导电油墨填料的研究进展[J].化工进展,2015,34(12):4259-4264.
[28]中国科学院宁波材料技术与工程研究所,芜湖春风新材料有限公司.一种石墨烯/丙烯酸导静电涂料及其制备方法:201610353311.5[P].2016–10–12.
[29]LIU S,GU L,ZHAO H C,et al.Corrosion resistance of graphene-reinforced waterborne epoxy coatings[J].Journal of Materials Science&Technology,2016,32(5):425-431.
[30]GU L,LIU S,ZHAO H C,et al.Facile preparation of water-dispersible graphene sheets stabilized by carboxylated oligoanilines and their anticorrosion coatings[J].ACS Applied Materials&Interfaces,2015,7(32):17641-17648.
[31]刘栓,姜欣,赵海超,等.石墨烯环氧涂层的耐磨耐蚀性能研究[J].摩擦学学报,2015,35(5):598-605.
[32]刘栓,赵霞,赵文杰.海水环境下石墨烯基重防腐涂层耐磨耐蚀机理研究[C]//中国腐蚀与防护协会.全国第八届腐蚀大会学术会议论文集.[出版地不详:出版者不详],2015:36-37.
[33]王玉琼,刘栓,刘兆平,等.石墨烯掺杂水性环氧树脂的隔水和防护性能[J].电镀与涂饰,2015,34(6):314-319.
[34]姜振华,赵东辉,林立民,等.铜粉填充的导电涂料[J].涂料工业,1992,22(3):12-13.
[35]施冬梅,鲁彦玲,杜仕国.偶联剂对铜-环氧电磁屏蔽导电涂料的影响[J].中国涂料,2005,20(6):16-18.
[36]申蓓蓓,郭忠诚.塑料件用水性导电涂料的研制[J].涂料工业,2007,37(7):26-28,31.
[37]张心华,闫爱军.富镍导电涂层耐腐蚀性能研究[J].涂料工业,2015,45(3):1-6.
[38]张松,李永,刘增堂.水性镍系电磁屏蔽涂料的制备及导电性能研究[J].电子元件与材料,2006,25(10):65-67.
[39]史政海,张群安.浅色复合导电涂料[J].中国涂料,2004,19(7):30-32.
[40]杜仕国,刘小强,闫军,等.纳米ATO复合导电涂料的研制[J].北京理工大学学报,2007,25(增刊1):285-287.
[41]杨华明,胡岳华,张慧慧.重晶石基锑掺杂Sn O2导电粉末用于导电涂料及其屏蔽特性[J].功能材料,2006,37(9):1433-1435.
[42]余凤斌,陈莹.镀银铜粉导电涂料的制备及性能[J].电镀与涂饰,2012,31(9):63-65.
[43]吕维华,伍家卫,唐蓉萍,等.高氯化聚乙烯银包铜防腐导电涂料的研究[J].中国建材科技,2012,21(1):63-67.
[44]李哲男,黄昊,张雪峰,等.导电涂料中纳米铜粉抗氧化性的研究[J].材料科学与工艺,2008,16(6):826-829,834.
[45]张露露,游敏,吴建好,等.玻璃鳞片导电涂料的研究[J].电镀与涂饰,2007,26(2):32-34.
[46]谭宁,郭忠诚.电解行业用环氧导电防腐涂料的制备[J].电镀与涂饰,2008,27(12):49-51,54.
[47]姜才兴,周福根,张晓凌.浅色油罐氟碳导静电防腐涂料的研制[J].中国涂料,2008,23(1):15-19.