摘要
采用原位聚合法制备磷酸氢锆/浇铸尼龙6(Zr(HPO_4)_2/MCPA6)复合材料。X射线衍射和差示扫描量热研究表明,当Zr(HPO_4)_2的质量分数为1.5%时,复合材料的结晶度由纯MCPA6的15.1%增加到22.2%,少量的Zr(HPO_4)_2对复合材料能起到结晶成核剂的作用,诱导γ(200)晶型的产生;偏光显微镜对复合材料等温结晶的观察进一步验证了上述对复合材料结晶度表征的结果。摆锤冲击试验和热重分析显示,随着Zr(HPO_4)_2的加入,复合材料的冲击强度和热稳定性有所增加。
The Zr(HPO_4)_2/MCPA6 composites were prepared by in-situ polymerization. The results of XRD and differential scanning calorimeter show that when the mass fraction of Zr(HPO_4)_2 is 1.5%, the crystallinity of the composites increases from 15.1% of pure MCPA6 to 22.2%, a little amount of Zr(HPO_4)_2 can play the role of crystallization nucleating agent and induce the production of γ(200) crystal; the observation of isothermal crystallization of composites by polarizing microscope further verifies the above results of crystallinity characterization of the composites. The pendulum impact test and thermogravimetric analysis show that the impact strength and thermal stability of the composites increase with the addition of Zr(HPO_4)_2 into the matrix.
引文
[1] 王海燕,韩大雄,相明辉,等.水溶性阳离子型卟啉对层状磷酸锆插层行为的研究[J].化学学报,2005,63(14):1361-1364.Wang H Y,Hang D X,Xiang M H,et al.Study on the Different Layered Zirconium Phosphates Hosts for Intercalating Soluble Cationic Porphyrins [J].Acta Chimica Sinica,2005,63(14):1361-1364.
[2] Picard E,Vermogen A,Gérard J F,et al.Barrier properties of nylon 6-montmorillonite nanocomposite membranes prepared by melt blending:influence of the clay content and dispersion state:consequences on modelling [J].J.Membr.Sci.,2007,292:133-144.
[3] 赖登旺,李笃信,杨军,等.脱水工艺对铸型尼龙6/蒙脱土纳米复合材料的影响[J].高分子材料科学与工程,2015,31(8):150-155.Lai D W,Li D X,Yang J,et al.Effects of dehydration process on cast nylon 6/montmorillonite nano-composites [J].Polymer Materials Science & Engineering,2015,31(8):150-155.
[4] 杜以波,张广积,孙鹏,等.α-磷酸锆层柱材料的制备、表征及其催化羰基化性能[J].催化学报,1999,20(2):145-149.Du Y B,Zhang G J,Sun P,et al.Preparation,characterization and catalytic carbonylation of -zirconium phosphate column materials [J].Journal of Catalysis,1999,20(2):145-149.
[5] Heng X,Xiang L,Li W,et al.Flame retardancy of polyamide 6 hybrid fibers:combined effects of α-zirconium phosphate and ammonium sulfamate [J].Prog.Nat.Sci.:Mater.Int.,2017,27:369-373.
[6] Zhang Y J,Zeng X R,Li H Q,et al.Zirconium phosphate functionalized by hindered amine:a new strategy for effectively enhancing the flame retardancy of addition-cure liquid silicone rubber [J].Mater.Lett.,2016,174:230-233.
[7] Xu S,Zhao X W,Ye L.Effect of heat treatment on the structure and properties of MC Nylon 6 [J].Polym.Plast.Technol.Eng.,2012,51:689-695.
[8] Han Z D,Qu C,Peng Y X,et al.Wear performance of rubber wheel of roller guide shoes[J].Adv.Mater.Res.,2010,113/114/115/116:1930-1934.
[9] Kohan M I.Nylon plastics handbook[M].New York:Hanser Publishers,1995.
[10] 何曼君.高分子物理[M].上海:复旦大学出版社,2011.
[11] 付绪兵.石墨烯/PA6纳米复合材料的制备、结构与性能[D].合肥:合肥工业大学,2016.Fu X B.Preparation,structure and properties of graphene /PA6 nanocomposites [D].Hefei:Hefei University of Technology,2016.
[12] Petrov P,Gancheva V,Philipova T,et al.Synthesis of nylon-6 triblock copolymers with bifunctional polymeric activators [J].J.Polym.Sci.Part A:Polym.Chem.,2015,38:4154-4164.
[13] 胡建民,王蕊,王春婷.晶体X射线衍射模型和布拉格方程的一般推导[J].大学物理,2015,34(3):1-2.Hu J M,Wang R,Wang C T.The crystal X-ray diffraction model and the general derivation of the Bragg equation [J].University Physics,2015,34(3):1-2.
[14] Hsiao B S,Gardner K C H,Wu D Q,et al.Time-resolved X-ray study of poly (aryl ether ether ketone) crystallization and melting behaviour:1.Crystallization[J].Polymer,1993,34:3986-3995.
[15] Blundell D J,Osborn B N.The morphology of poly(aryl-ether-ether-ketone)[J].Polymer,1983,24:953-958.