摘要
以市售玉米淀粉为原料,以环氧氯丙烷为交联剂制备交联淀粉。通过研究不同反应条件对交联度的影响设计单因素试验。再通过离心测定其交联度,在单因素试验结果的基础上设计正交试验。通过四因素四水平正交试验确定交联淀粉的最佳工艺参数为:环氧氯丙烷为4.0m L、Na OH用量为4.0m L、反应时间为2.5h、反应温度40℃时交联度是最大的,影响交联淀粉合成顺序为:反应温度>环氧氯丙烷用量>反应时间>氢氧化钠用量。
The cross linked starch was prepared by using corn starch as material and epichlorohyd-rin as cross linker.The single factor experiments were designed by studying the degree of cross linker in the different reaction conditions.Then the degree of cross linker was measured by centrifuging.The orthogonal test was designed on the basis of the results about single factor experiments.The results of orthogonal test showed that dosage of epichlorohydrin 3.0m L,dosage of sodium hydroxide 3m L, reaction time 2.5h, reaction temperature 40℃.The influence on preparating cross linked starch in descreasing order was reaction temperature > dosage of epichlorohydrin > reaction time > dosage of sodium hydroxide.
引文
[1]张燕萍.变性淀粉制造与应用[M].北京:化学工业出版社,2001:61-63.
[2]王建新.淀粉衍生物的制备及在造纸工业中的应用[J].天津造纸.2006(4):32-35.
[3]唐凤华,杨汝男,龚业熊.几种改性淀粉对提高纸张干强度的效果比较[J].纸和造纸,2003(4):34-36.
[4]刘宝贵,慈元钊.淀粉增强剂在胶版印刷纸上的应用[J].湖南造纸.2002(1):22-23.
[5]张光华,王卓妮,朱军峰.氧化醋酸酯淀粉的制备及其在表面施胶中的应用[J].中国造纸,2006(3):15-17.
[6]张继良.交联羟丙基复合变性淀粉制备及性能研究[D].沈阳:沈阳工业大学,2005.
[7]马冰洁,罗杨,唐洪波,等.不溶性淀粉黄原酸酯的制备[J].淀粉工程技术,2009(12):131-134.
[8]孙阿惠,柳莹,苏敏,等.微波干法制备醚化淀粉絮凝剂及其应用[J].工业用水与废水,2011,42(4):69-71.
[9]李芳良,童张法,麻昌爱.食用木薯交联-氧化复合变性淀粉制备[J].食品研究与开发,2009,30(9):61-64.
[10]周睿,曹龙奎,包鸿慧.交联羧甲基玉米淀粉的制备及其微观结构研究[J].粮油加工,2009(1):103-109.
[11]孔令晓,崔波,赵京敏.高交联改性淀粉的制备及性质研究[J].食品与发酵科技,2009,45(5):45-47.
[12]徐忠,周美琴,杨雪欣,等.复合交联玉米淀粉的制备工艺及特性研究[J].中国粮油学报,2009,24(5):40-43.
[13]王春艳.甘薯氧化交联淀粉的制备及其性质研究[D].重庆:西南大学,2008:49-55.
[14]石海信,谢新玲,张友全,等.醚化交联玉米辛烯基琥珀酸淀粉酯的制备工艺及特性[J].食品科技,2009,34(8):214-217.
[15]孙吉,韩育梅.丁二酸马铃薯淀粉酯的合成及性质研究[J].中国粮油学报,2010,25(1):47-50.