热轧带肋钢筋产品质量比对分析
|
摘要
采集了省内外具有代表性的钢企生产的?16 mm规格HRB400E热轧带肋钢筋,按照国标GB/T 1499.2-2007A1和GB/T 1499.2-2018规定进行检测。比较了各厂的产品性能差异,分析了不合格项目的成因,提出了质量改进建议。
The specification of 16 mm hot rolled ribbed bar HRB400 E produced by representative steel enterprises in and outside Guangdong Province has been collected and tested according to the provisions of GB/T 1499.2-2007 A1 and GB/T 1499.2-2018. The product performance differences of various factories have been compared, the causes of unqualified items have been analyzed, and quality improvement suggestions have been put forward.
The specification of 16 mm hot rolled ribbed bar HRB400 E produced by representative steel enterprises in and outside Guangdong Province has been collected and tested according to the provisions of GB/T 1499.2-2007 A1 and GB/T 1499.2-2018. The product performance differences of various factories have been compared, the causes of unqualified items have been analyzed, and quality improvement suggestions have been put forward.
引文
[1]中华人民共和国国家统计局-国家数据-年度数据-指标-工业-工业产品产量-钢材产量(万吨)/钢筋产量(万吨)-时间:2015~2018共4个年度选项[ER/OL].http://data.stats.gov.cn/easyquery.htm?cn=C01.
[2]粤质监监函[2018]234号.广东省质监局关于报送产品质量比对研究提升项目的通知[Z].广州:广东省质量技术监督局,2018.
[3]徐框迪,洪新.电炉短流程回顾和发展中的若干问题[J].中国冶金,2005,15(7):1-8.
[4]完卫国,杨仁江.英标460 MPa级钢筋余热处理工艺研究[J],山东冶金,2005,27(5):35-38.
[5][英]R.W.卡恩.物理金属学(中册)[M],北京:科学出版社,1984:732-734.
[6]张志强,李新华,李克让.Ⅱ级螺纹钢反弯性能研究[J].河北冶金,2001,125(5):16-18.
[7]潘建洲.螺纹钢冷弯性能与横肋形状的研究与应用[J].钢铁.2005,40(8):53-55.
[6]雷三祥,彭其春,王友华.HRB400螺纹钢冷弯断裂的原因分析[J].热加工工艺,2017 46(7):246-248.
[9]罗云蓉,王清远,于强.HRB400Ⅲ级抗震钢筋的低周疲劳性能[J].钢铁研究学报.2015,27(6):35-39.
[10]陈传尧.疲劳与断裂[M].武汉:华中科技大学出版社,2001:114.
[11]曹靖涛,关桂芬.广东省建筑钢材产品质量状况报告[R],广东省产品质量状况分析报告(2013-2016年)(下册).广州:广东省质量技术监督局,2017:299-309.
[12]中国质量新闻网责任编辑.热轧带肋钢筋产品抽查合格率为95.3![EB/OL].中国质量新闻网,http://www.cqn.com.cn/ms/content/2014-10/29/content_2331104.htm,2014-10-29.
[13]中国质量新闻网责任编辑.质检总局抽查钢筋混凝土用热轧带肋钢筋8批次不合格[EB/OL].中国质量新闻网,http://www.cqn.com.cn/ms/content/2015-08/27/content_2545216.htm,2015-08-27.
[14]中国质量新闻网责任编辑.质检总局抽查:3批次钢筋混凝土用热轧带肋钢筋产品不符合标准规定[EB/OL].中国质量新闻网,http://www.cqn.com.cn/ms/content/2016-03/15/content_2663378.htm 2016-03-15.
[15]八雨.质检总局抽查钢筋混凝土用热轧带肋钢筋产品全部合格[EB/OL].中国质量新闻网,http://www.cqn.com.cn/ms/content/2017-12/05/content_5173694.htm,2017-12-05.
[16]六六.市场监管总局抽查118批次热轧带肋钢筋产品不合格3批次[EB/OL].中国质量新闻网,http://www.cqn.com.cn/ms/content/2018-09/21/content_6283357.htm,2018-09-21.
[2]粤质监监函[2018]234号.广东省质监局关于报送产品质量比对研究提升项目的通知[Z].广州:广东省质量技术监督局,2018.
[3]徐框迪,洪新.电炉短流程回顾和发展中的若干问题[J].中国冶金,2005,15(7):1-8.
[4]完卫国,杨仁江.英标460 MPa级钢筋余热处理工艺研究[J],山东冶金,2005,27(5):35-38.
[5][英]R.W.卡恩.物理金属学(中册)[M],北京:科学出版社,1984:732-734.
[6]张志强,李新华,李克让.Ⅱ级螺纹钢反弯性能研究[J].河北冶金,2001,125(5):16-18.
[7]潘建洲.螺纹钢冷弯性能与横肋形状的研究与应用[J].钢铁.2005,40(8):53-55.
[6]雷三祥,彭其春,王友华.HRB400螺纹钢冷弯断裂的原因分析[J].热加工工艺,2017 46(7):246-248.
[9]罗云蓉,王清远,于强.HRB400Ⅲ级抗震钢筋的低周疲劳性能[J].钢铁研究学报.2015,27(6):35-39.
[10]陈传尧.疲劳与断裂[M].武汉:华中科技大学出版社,2001:114.
[11]曹靖涛,关桂芬.广东省建筑钢材产品质量状况报告[R],广东省产品质量状况分析报告(2013-2016年)(下册).广州:广东省质量技术监督局,2017:299-309.
[12]中国质量新闻网责任编辑.热轧带肋钢筋产品抽查合格率为95.3![EB/OL].中国质量新闻网,http://www.cqn.com.cn/ms/content/2014-10/29/content_2331104.htm,2014-10-29.
[13]中国质量新闻网责任编辑.质检总局抽查钢筋混凝土用热轧带肋钢筋8批次不合格[EB/OL].中国质量新闻网,http://www.cqn.com.cn/ms/content/2015-08/27/content_2545216.htm,2015-08-27.
[14]中国质量新闻网责任编辑.质检总局抽查:3批次钢筋混凝土用热轧带肋钢筋产品不符合标准规定[EB/OL].中国质量新闻网,http://www.cqn.com.cn/ms/content/2016-03/15/content_2663378.htm 2016-03-15.
[15]八雨.质检总局抽查钢筋混凝土用热轧带肋钢筋产品全部合格[EB/OL].中国质量新闻网,http://www.cqn.com.cn/ms/content/2017-12/05/content_5173694.htm,2017-12-05.
[16]六六.市场监管总局抽查118批次热轧带肋钢筋产品不合格3批次[EB/OL].中国质量新闻网,http://www.cqn.com.cn/ms/content/2018-09/21/content_6283357.htm,2018-09-21.