高压热处理对耐磨高锰钢硬度的影响
|
摘要
研究了高压热处理对耐磨高锰钢硬度的影响。结果表明:高压热处理能有效提高耐磨高锰钢的硬度。铸态耐磨高锰钢经1050℃×60 min的固溶处理+4 GPa压力下500℃×15 min的高压热处理后的硬度为512 HV,较耐磨高锰钢固溶处理后的硬度提高了155%。
The effect of high pressure heat treatment on hardness of wear-resistant high manganese steel was studied. The results show that, high pressure heat treatment can effectively improve the hardness of wear resistant high manganese steel.The hardness of cast wear-resistant high manganese steel solution treated with 1050 ℃×60 min and treated at 500 ℃×15 min under high pressure of 4 GPa is 512 HV. Compared with that of wear-resistant high manganese steel, the hardness increases by155% after solution treatment.
The effect of high pressure heat treatment on hardness of wear-resistant high manganese steel was studied. The results show that, high pressure heat treatment can effectively improve the hardness of wear resistant high manganese steel.The hardness of cast wear-resistant high manganese steel solution treated with 1050 ℃×60 min and treated at 500 ℃×15 min under high pressure of 4 GPa is 512 HV. Compared with that of wear-resistant high manganese steel, the hardness increases by155% after solution treatment.
引文
[1]宋仁伯,冯一帆,彭世广,等.高锰钢衬板的研究及应用[J].材料导报,2015,29(10):74-77.
[2]吴化,徐珊珊,王淮.变质和时效处理对ZGMn13高锰钢力学性能的影响[J].金属热处理,2009,34(9):78-82.
[3]李威,黄圣玲,马歆.低温时效工艺对高锰钢组织和力学性能的影响[J].热处理技术与装备,2015,36(6):49-53.
[4]吴化,徐珊珊.多元变质处理对高锰钢微观结构与性能的影响[J].铸造,2008,57(1):66-68.
[5]施忠良,张守年.高锰钢的合金化组织及加工硬化性能[J].材料科学与工艺,1993,l(6):22-27.
[6]刘志学,程巨强.不同形变对高锰钢组织和性能的影响[J].铸造,2008,57(6):1287-1289.
[7]严伟林.高锰钢在喷丸条件下的应变硬化[J].装备制造技术,2008,25(4):32-33.
[8]高波,杨攀,王剑.时效处理对高锰钢组织及耐磨性能的影响[J].热加工工艺,2016,45(2):192-195.
[9]刘世永,史雅琴,季世军.碳化物弥散分布耐磨高锰钢[J].机械工程材料,1996,20(4):18-19.
[10]胡晓艳,沈兆武,刘天生,等.基体对高锰钢辙叉爆炸硬化效果的影响[J].工程爆破,2015,21(2):48-50.
[11]李兴霞,赵干,张观军.高锰钢爆炸硬化机理分析[J].热加工工艺,2013,42(6):94-96.
[12]曹栋,刘建强,冯仑仑,等.3 GPa压力热处理对TC6钛合金的硬度和抗压强度的影响[J].金属热处理,2015,40(7):25-27.
[13]赵军,尹硕,陈久川,等.高压处理对Cu-50.84Cr-0.48Al合金热扩散系数和热膨胀性能的影响[J].稀有金属,2013,37(5):834-839.
[14]Wang Y H, Zhao J, Liu J H, et al.Effect of high pressure heat treatment on microstructures and micro-mechanical properties of CuZn alloy[J].High Temperature Materials and Processes,2014,33(4):339-344
[15]丁志敏,王树娟,杨芳,等.高锰钢低温时效处理时的组织结构[J].材料热处理学报,2007,28(s):29-32.
[16]严伟林,方亮,郑战光.高锰钢加工硬化[J].铸造技术,2008,29(11):1468-1472.
[2]吴化,徐珊珊,王淮.变质和时效处理对ZGMn13高锰钢力学性能的影响[J].金属热处理,2009,34(9):78-82.
[3]李威,黄圣玲,马歆.低温时效工艺对高锰钢组织和力学性能的影响[J].热处理技术与装备,2015,36(6):49-53.
[4]吴化,徐珊珊.多元变质处理对高锰钢微观结构与性能的影响[J].铸造,2008,57(1):66-68.
[5]施忠良,张守年.高锰钢的合金化组织及加工硬化性能[J].材料科学与工艺,1993,l(6):22-27.
[6]刘志学,程巨强.不同形变对高锰钢组织和性能的影响[J].铸造,2008,57(6):1287-1289.
[7]严伟林.高锰钢在喷丸条件下的应变硬化[J].装备制造技术,2008,25(4):32-33.
[8]高波,杨攀,王剑.时效处理对高锰钢组织及耐磨性能的影响[J].热加工工艺,2016,45(2):192-195.
[9]刘世永,史雅琴,季世军.碳化物弥散分布耐磨高锰钢[J].机械工程材料,1996,20(4):18-19.
[10]胡晓艳,沈兆武,刘天生,等.基体对高锰钢辙叉爆炸硬化效果的影响[J].工程爆破,2015,21(2):48-50.
[11]李兴霞,赵干,张观军.高锰钢爆炸硬化机理分析[J].热加工工艺,2013,42(6):94-96.
[12]曹栋,刘建强,冯仑仑,等.3 GPa压力热处理对TC6钛合金的硬度和抗压强度的影响[J].金属热处理,2015,40(7):25-27.
[13]赵军,尹硕,陈久川,等.高压处理对Cu-50.84Cr-0.48Al合金热扩散系数和热膨胀性能的影响[J].稀有金属,2013,37(5):834-839.
[14]Wang Y H, Zhao J, Liu J H, et al.Effect of high pressure heat treatment on microstructures and micro-mechanical properties of CuZn alloy[J].High Temperature Materials and Processes,2014,33(4):339-344
[15]丁志敏,王树娟,杨芳,等.高锰钢低温时效处理时的组织结构[J].材料热处理学报,2007,28(s):29-32.
[16]严伟林,方亮,郑战光.高锰钢加工硬化[J].铸造技术,2008,29(11):1468-1472.